The possibility to change magnetic anisotropy of amorphous TbCo films from out-of-plane to in-plane has been investigated. The effects of TbCo film's thickness and composition on the magnetic anisotropy were investigated together with the effects of growing the TbCo films on a SmCo seed layer. This was studied by sputtering TbCo films of composition Tb_xCo_(100-x) x=16,18,20,22 and 24, with thickness ranging between 2-20 nm, with and without the presence of a 20 nmSm_15Co_85 seed layer. All films were grown in a 130 mT magnetic in-plain field to imprint an in-plane anisotropy. The structure and composition of the films were examined with Rutherford backscattering spectrometry, X-ray reflectivity, and Grazing incidence X-ray diffraction. The magnetic properties of the films were studied with magneto-optic Kerr effect measurement, vibrating sample magnetometer, Kerr microscopy and magnetic force microscopy. The magneto-optic Kerr effect measurement showed that it was possible to change TbCo film's preferred magnetization direction from out-of-plane to in-plane by reducing the film thickness. The SmCo layer made it easier for theTbCo films to change preferred magnetization direction from out-of-plane to in-plane.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-348209 |
Date | January 2018 |
Creators | Djurberg, Viktor |
Publisher | Uppsala universitet, Materialfysik |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | UPTEC Q, 1401-5773 ; 18001 |
Page generated in 0.0091 seconds