Thin film solar cells of Copper Indium Telluride and Cadmium Sulfide junctions were fabricated on plain ITO glass slides and also on those coated with intrinsic Tin Oxide. CdS was deposited through chemical bath deposition and CIT by electrodeposition. Both compounds were subjected to annealing at temperatures between 350°C and 500°C which produced more uniform film thicknesses and larger grain sizes. The CIT/ CdS junction was characterized after performing XRD and spectral absorption of individual compounds.
Studies were also made on CdS / CdTe solar cells with respect to effect of annealing temperatures on open circuit voltages. NP acid etch, the most important process to make the surface of CdTe tellurium rich, was also studied in terms of open circuit voltages. Thermally evaporated CdS of four different thicknesses was deposited on Tin Oxide coated ITO and inferences were drawn as to what thickness of CdS yields better results.
| Identifer | oai:union.ndltd.org:uky.edu/oai:uknowledge.uky.edu:gradschool_theses-1654 |
| Date | 01 January 2011 |
| Creators | Gutta, Venkatesh |
| Publisher | UKnowledge |
| Source Sets | University of Kentucky |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | University of Kentucky Master's Theses |
Page generated in 0.0017 seconds