Estabilidade e metaestabilidade de fases em ligas Ti-Nb / Stability and metastability of phases in Ti-Nb alloys

Orientadores: Rubens Caram Junior, Conrado Ramos Moreira Afonso / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-06T17:14:04Z (GMT). No. of bitstreams: 1
Aleixo_GiorgiaTaiacol_M.pdf: 13698827 bytes, checksum: 10117398b384c5a1eda6c62fbfc74507 (MD5)
Previous issue date: 2006 / Resumo: Ligas de titânio formam a classe mais versátil de materiais metálicos utilizados para aplicações biomédicas. As ligas de Ti tipo ß usadas em dispositivos ortopédicos envolve, além de excelentes propriedades como baixa densidade, elevada resistência mecânica e excepcional resistência à corrosão, a biocompatibilidade com elementos de liga, tais como Nb, Ta, Zr e Mo. O objetivo deste trabalho foi analisar a estabilidade e metaestabilidade de fases em ligas tipo ß no sistema Ti-Nb através da verificação da influência do teor de nióbio sob diversas condições de tratamento térmico. Para tanto variou-se a adição de Nb de 5% a 30% em peso na liga, obtendo amostras que foram submetidas a condições distintas de resfriamento a partir do campo ß. Amostras obtidas foram caracterizadas no tocante à microestrutura via microscopia ótica, eletrônica de varredura e de transmissão, difração de raios-X, enquanto o comportamento mecânico foi preliminarmente avaliado através de ensaios de dureza Vickers e de medidas de módulo de elasticidade através de técnicas acústicas. Os resultados obtidos indicam que baixas taxas de resfriamento conduzem à microestrutura de equilíbrio (a+ß) enquanto que altas taxas de resfriamento levaram à formação de estruturas metaestáveis. À medida que o teor de Nb foi incrementado e sob altas taxas de resfriamento, obteve-se, respectivamente, martensita a¿ (hexagonal compacta), martensita a¿ (ortorrômbica), fase ? (trigonal) e finalmente, fase ß metaestável. Em relação ao módulo de elasticidade, observou-se que esse parâmetro decresce entre 0 e 15% de Nb e após este último valor, tal constante elástica se eleva como resultado da precipitação de fase ? bem como da possível alteração de dimensões da estrutura cristalina. As ligas Ti-Nb apresentaram uma variabilidade de microestruturas e propriedades que dependem fortemente da composição e condição de resfriamento / Abstract: Titanium alloys form one of the most versatile classes of metallic materials used for biomedical applications. ß Ti alloys for orthopaedic devices involves, besides excellent properties like low density, high mechanical strength and good corrosion resistance, great biocompatibility with alloying elements, such as Nb, Ta, Zr and Mo. The objective of this work was to analyze the stability and metastability of phases in ß Ti-Nb alloys through the evaluation of the influence of percentage of Nb obtained in different heat treatment conditions. In this way, Nb addition was varied from 5 to 30wt% in Ti-Nb system. Samples were obtained and microstructural characterization was made through optical microscopy, scanning and transmission electron microscopy and X-ray diffraction, while mechanical behavior was primarily evaluated by Vickers hardness and elasticity modulus through acoustic techniques. The results obtained indicate that lower cooling rates resulted in the equilibrium microstructures (a+ß), otherwise higher cooling rates led to formation of metastable structures. As the Nb content was increased and under greater cooling rates, it was obtained, respectively, martensite a¿ (hexagonal closed packed), martensite a¿ (orthorhombic), ? phase (trigonal) and finally, metastable ß phase. Regarding modulus of elasticity it was observed that it decreases as the %Nb increases up to 15% and beyond this percentage the modulus increases due the precipitation of ? phase as well as possible variation of crystalline structure dimensions. Ti-Nb alloys presented a great variety of combinations between microstructures and properties that strongly depends on composition and cooling conditions / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263173
Date16 February 2006
CreatorsAleixo, Giorgia Taiacol
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Afonso, Conrado Ramos Moreira, Caram Junior, Rubens, 1958-, Junior, Rubens Caram, Santos, Rezende Gomes dos, Grandini, Carlos Roberto
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format103p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.002 seconds