Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Ciência e Engenharia de Materiais / Made available in DSpace on 2012-10-25T17:46:04Z (GMT). No. of bitstreams: 1
301079.pdf: 2153946 bytes, checksum: 58cb489646783a932f7ed533f416c2ac (MD5) / Os compósitos poliméricos, em especial polímeros reforçados com fibras vegetais, se comparados com outros materiais poliméricos ou mesmo metais, possuem baixa densidade e alta resistência específica, o que os torna adequados para serem utilizados principalmente nas indústrias automotiva, moveleira e de construção civil. Estes materiais também apresentam como vantagens baixo custo e sustentabilidade devido à utilização das fibras vegetais que são provenientes de fontes renováveis. Dentre as diversas plantas fibrosas que fornecem fibras vegetais aplicáveis em compósitos, a grande maioria pode ser cultivada no Brasil, podendo-se destacar os bambus. Além das inúmeras utilizações do bambu como material de construção e matéria prima industrial, é possível extrair suas fibras e utilizá-las como reforço em compósitos. Neste trabalho foram desenvolvidos compósitos de matriz epóxi ou poliuretano derivado do óleo de mamona com fibras de bambu através do processo de laminação manual seguido de moldagem por compressão. Laminados contínuos de bambu foram extraídos pelo processo de torneamento utilizando-se um dispositivo desenvolvido e construído em laboratório. As propriedades mecânicas dos compósitos foram avaliadas através dos ensaios de tração, flexão, impacto e análise dinâmico-mecânica. A microestrutura dos bambus, dos laminados e dos compósitos foi analisada por Microscopia Óptica e Eletrônica de Varredura. Os compósitos obtidos neste trabalho apresentaram baixa densidade e excelentes propriedades mecânicas de tração, flexão e impacto. Suas propriedades específicas são quase cinco vezes à de um aço baixo carbono e comparáveis às propriedades de compósitos de fibras de vidro. Os compósitos obtidos possuem propriedades adequadas para serem utilizados em diversas aplicações tecnológicas, principalmente nos setores automotivo, moveleiro e de construção civil. / Polymer composites, especially vegetable fiber reinforced polymers, have low density and adequate specific strength to be used in the automotive, furniture and civil construction industries. These are low cost and sustainable materials produced with vegetable fibers which are renewable sources. Among the innumerous plants from which biofibers are produced, most of them can be grown and cultivated in Brazil especially the bamboos. Besides the utilization of bamboo as a construction material and industrial raw material, it is also possible to extract its fibers and use them as reinforcement in composites. Polymer matrix composites made from polyurethane or epoxy resin reinforced with bamboo veneers were developed in this work using the hand layup technique followed by compression molding. It was used a castor oil derived polyurethane resin which comes from renewable sources. Rotary cut continuous bamboo veneers were extracted through an especially designed apparatus which was developed and constructed in laboratory. The composites mechanical properties were evaluated by tensile, flexural and impact testing, as well as the dynamic-mechanical analysis. The bamboo microestructure was evaluated by optical and scanning electron microscopy. Composites obtained in this work presented low density and excellent tensile, flexural and impact strengths. Its specific properties were almost five times greater than low carbon steel and even comparable to fiber glass reinforced composites. The composites have adequate properties to be used in innumerous technological applications, especially in the automotive, furniture and construction sectors.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/94902 |
| Date | January 2011 |
| Creators | Targa, Gabriel Norcia e |
| Contributors | Universidade Federal de Santa Catarina, Barra, Guilherme Mariz de Oliveira, Qureshi, Hazim Ali Al- |
| Publisher | Florianópolis, SC |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 106 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds