Previous issue date: 2007-02-22 / CNPq / Membranas obtidas por sinterização de partículas de PEUAPM foram desenvolvidas visando sua aplicação no tratamento de efluentes. As membranas foram sinterizadas em diferentes tempos e temperaturas e o seu desempenho na remoção de partículas presentes em efluentes aquosos foi investigado. Utilizou-se o planejamento experimental fatorial e análise de superfície de resposta para avaliar os efeitos do tempo e temperatura de sinterização no desempenho das membranas. Este estudo foi conduzido com as amostras que apresentaram menor tamanho de partículas, isto é, passantes em peneira de malha 200. Os resultados evidenciam que quanto maiores os tempos e temperaturas de sinterização, menores os fluxos do permeado através das membranas e que os efeitos da temperatura foram mais acentuados do que os do tempo de sinterização. A compactação das membranas após a sinterização provocou reduções no fluxo e na porosidade, enquanto o tamanho médio dos poros permaneceu inalterado. Dois procedimentos foram utilizados para modificar a superfície interna das membranas: a) deposição de um filme de PEAD e b) modificação por plasma de metano. Estas modificações foram realizadas nas membranas manufaturadas com pó de PEUAPM como recebidos do fabricante e com os passantes em peneira de malha 200. Ambas as modificações de superfície levaram a reduções no tamanho de poros na superfície das membranas. O tratamento por plasma minimizou o fenômeno de “fouling”, enquanto que maior eficiência na remoção de partículas sólidas em suspensão na água foi obtida
com membranas recobertas internamente com filme de PEAD. Melhor desempenho global foi obtido para as membranas manufaturadas com PEUAPM de código 3041 passante em peneira de malha 200, superficialmente modificadas ou não. Este estudo indica que o PEUAPM pode ser usado na produção de membranas de microfiltração de baixo custo para remoção de partículas sólidas presentes em efluentes aquosos. / Membranes obtained by sintering of UHMWPE powders were manufactured aiming at their use in effluent treatment. The membranes were sintered at different times and temperatures and their performance in aqueous effluent particle removal were investigated. An factorial experimental planning and response surface analysis was employed to evaluate the effects of sintering time and temperature in the performance of the membranes. This study was conducted on samples having the smallest particles size, i.e., with powders that passed through a 200 mesh sieve. Higher sintering times and temperatures led to smaller permeate flow through membranes and temperature effects were more significant than those of time. Membranes compaction after sintering leads to lower permeate flows and porosities, although the average pore sizes do not change. Two routes were used to modify the internal surface of the membranes: a) HDPE film deposition and b) methane plasma modification.These modifications were made with membranes prepared with UHMWPE powder as received from supplier and passed through a 200 mesh sieve. Both treatments caused reductions on the membranes superficial pore sizes. Plasma treatment minimized the “fouling” phenomenon, while the best efficiency in solid particle removal from water dispersions was found for the membrane internally coated with a HDPE film. Best overall performances were displayed by the membranes prepared with UHMWPE grade 3041 sieved though a 200 mesh sieve. The results indicate that the UHMWPE can be used to prepare low cost micro-filtration membranes to remove solid particles present in aqueous effluents.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1914 |
| Date | 08 October 2018 |
| Creators | LEAL, Tânia Lúcia. |
| Contributors | CARVALHO, Laura Hecker de., LIRA, Hélio Lucena de., ALVES JÚNIOR, Clodomiro., GARCIA, Rosângela Balaban., ARAÚJO, Edcleide Maria., MELO, Tomás Jefferson Alves de. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0038 seconds