In this work a manufacturing method for UN, ZrN and (U,Zr)N pellets was established at the nuclear fuel laboratory at KTH Stockholm/Sweden, which consists of the production of nitride powders and their sintering into pellets by spark plasma sintering. The nitride powders were produced by the hydriding-nitriding route using pure metal as starting material. This synthesis was performed in a stream of the particular reaction gas. A synthesis control and monitoring system was developed, which can follow the reactions in real time by measuring the gas flow difference before and after the reaction chamber. With the help of this system the hydriding and nitriding reactions of uranium and zirconium were studied in detail. Fine nitride powders were obtained; however, the production of zirconium nitride involved one milling step of the brittle zirconium hydride. Additionally uranium and zirconium alloys with different zirconium contents were produced and synthesized to nitride powders. It was found that also the alloys could be reduced to fine powder, but only by cyclic hydriding-dehydriding. Pellets were sintered out of uranium nitrides, zirconium nitrides, mixed nitrides and alloy nitrides. These experiments showed that relative densities of more than 90% can easily be achieved for all those powders. Pellets sintered from mechanically mixed nitride powders were found to still consist of two separate nitride phases, while nitride produced from alloy was demonstrated to be a monophasic solid solution both as powder and as sintered pellets.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-35249 |
Date | January 2011 |
Creators | Hollmer, Tobias |
Publisher | KTH, Fysik |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Trita-FYS, 0280-316X ; 2011:32 |
Page generated in 0.0082 seconds