Abstract
Ammonia is one of valuable chemicals which are commonly used in various industrial factors. It is also a typical pollutant, and has a long-term impact on human health for toxicity characteristics. This study was to investigate the performance, product selectivity and kinetics in oxidation of ammonia solution in WAO process over Cu/ACF catalyst. The operation parameters in continuous WAO process were performed as follows: initial concentration of ammonia in ranging from 200 ppm to 1000 ppm, pH at 12, velocity of influent at below 3.0 ml/min, temperature ranging from 443K to 463K and pressure at 3.0 MPa.
In the experiments of catalyst selection, we decided to use 5% Cu/ACF catalyst for its high conversion and selectivity in oxidation of ammonia. A conversion of 95.42% in oxidation of ammonia was achieved under 463K and the product selectivity of N2 was raised from 53% to 85%. We found that Cu/ACF and ACF catalysts both had the good conversion and selectivity in oxidation of ammonia in WAO process.
In the long-term test of catalyst stability, Cu/ACF had a bad stability after 48 hours reaction in WAO process. The tests such as XRD, SEM and EA were also determined. The kinetics of WAO over Cu/ACF catalyst in oxidation of ammonia using Power-Rate Law was presented. The apparent reaction order and activated energy were obtained.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0623103-125411 |
| Date | 23 June 2003 |
| Creators | Chen, Kuan-Hung |
| Contributors | Ming-Shean Chou, Jimmy C. M. Kao, Jie-Chung Lou |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0623103-125411 |
| Rights | withheld, Copyright information available at source archive |
Page generated in 0.0014 seconds