An environmentally friendly, and contamination free process for etching and cleaning semiconductors is critical to future of the IC industry. Under the right conditions, water has the ability to meet these requirements. Water becomes more reactive as a function of temperature in part because the number of hydronium and hydroxyl ions increase. As water approaches its boiling point, the concentration of these species increases over seven times their concentrations at room temperature. At 150 °C, when the liquid state is maintained, these concentrations increase 15 times over room temperature. Due to its enhanced reactivity, high temperature water (HTW) has been studied as an etch and clean of thermally grown SiO2, Si3N4, and low-k films. High temperature deuterium oxide (HT-D2O) behaves similarly to HTW; however, it dissociates an order of magnitude less than HTW resulting in an equivalent reduction in reactive species. This allowed for the effects of reactive specie concentration on etch rate to be studied, providing valuable insight into how HTW compares to other high temperature wet etching processes such as hot phosphoric acid (HPA). Characterization was conducted using Fourier transform infrared spectroscopy (FTIR) to determine chemical changes due to etching, spectroscopic ellipsometry to determine film thickness, profilometry to measure thickness change across the samples, scanning electron microscopy (SEM), contact angle to measure changes in wetting behavior, and UV-Vis spectroscopy to measure dissolved silica in post etch water. HTW has demonstrated the ability to effective etch both SiO2 and Si3N4, HT-D2O also showed similar etch rates of Si3N4 indicating that a threshold reactive specie concentration is needed to maximize etch rate at a given temperature and additional reactive species do not further increase the etch rate. Because HTW has no hazardous byproducts, high temperature water could become a more environmentally friendly etchant of SiO2 and Si3N4 thin films.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc1404614 |
| Date | 12 1900 |
| Creators | Barclay, Joshua David |
| Contributors | Reidy, Richard F., Aouadi, Samir, Mukherjee, Sundeep |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | vii, 52 pages, Text |
| Rights | Public, Barclay, Joshua David, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0025 seconds