The surface chemistry of the bis(tri-n-butylphosphane) copper(I) acetylacetonate, [(nBu3P)2Cu(acac)], and the thermal atomic layer deposition (ALD) of Cu2O using this Cu precursor as reactant and wet oxygen as co-reactant on SiO2 substrates are studied by in-situ X-ray photoelectron spectroscopy (XPS). The Cu precursor was evaporated and exposed to the substrates kept at temperatures between 22 °C and 300 °C. The measured phosphorus and carbon concentration on the substrates indicated that most of the [nBu3P] ligands were released either in the gas phase or during adsorption. No disproportionation was observed for the Cu precursor in the temperature range between 22 °C and 145 °C. However, disproportionation of the Cu precursor was observed at 200 °C, since C/Cu concentration ratio decreased and substantial amounts of metallic Cu were present on the substrate. The amount of metallic Cu increased, when the substrate was kept at 300 °C, indicating stronger disproportionation of the Cu precursor. Hence, the upper limit for the ALD of Cu2O from this precursor lies in the temperature range between 145 °C and 200 °C, as the precursor must not alter its chemical and physical state after chemisorption on the substrate. 500 ALD cycles with the probed Cu precursor and wet O2 as co reactant were carried out on SiO2 at 145 °C. After ALD, in situ XPS analysis confirmed the presence of Cu2O on the substrate. Ex-situ spectroscopic ellipsometry indicated an average film thickness of 2.5 nm of Cu2O deposited with a growth per cycle of 0.05 Å/cycle. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) investigations depicted a homogeneous, fine, and granular morphology of the Cu2O ALD film on SiO2. AFM investigations suggest that the deposited Cu2O film is continuous on the SiO2 substrate.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:ch1-qucosa-147058 |
| Date | 07 July 2014 |
| Creators | Dhakal, Dileep, Waechtler, Thomas, E. Schulz, Stefan, Gessner, Thomas, Lang, Heinrich, Mothes, Robert, Tuchscherer, Andre |
| Contributors | TU Chemnitz, Center for Microtechnologies, TU Chemnitz, Institute of Chemistry, Fraunhofer ENAS, |
| Publisher | Universitätsbibliothek Chemnitz |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:article |
| Format | application/pdf, text/plain, application/zip |
| Source | http://scitation.aip.org/content/avs/journal/jvsta/32/4/10.1116/1.4878815?aemail=author |
Page generated in 0.0024 seconds