Previous issue date: 2018-01-12 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Com o avanço da ciência e processamento de materiais, a zircônia odontológica deixou de ser um material opaco para apresentar certa translucidez, possibilitando a confecção de peças ultrafinas. Sabe-se que a água em contato com a superfície das zircônias convencionais acarreta na transformação de fase T-M e subsequente decréscimo de resistência, mas esses efeitos nas zircônias translúcidas ainda não foram explorados. Para avaliar, mapear e caracterizar os efeitos da cinética de envelhecimento acelerado em zircônias de alta translucidez, foram cortados 39 blocos de Y-TZP (VITA YZ, VITA HT, InCoris TZI) para cada zircônia comercial, onde posteriormente foram sinterizados (1530 ºC, 2h) e atribuídos a 13 grupos com 3 amostras cada: Um controle e 12 envelhecidos hidrotermicamente a 134 ºC com pressão constante de 2 bars por 6, 10, 14, 18, 22, 26, 30, 40, 60, 80, 100 e 140 horas. A análise em DRX foi utilizada para quantificar a transformação de fase da zircônia (tetragonal-monoclínica) em diferentes profundidades do material ao se trocar o ânodo do tubo irradiador (Cr, Co e Cu). Uma curva cinética de envelhecimento foi feita para cada profundidade para as 3 zircônias comerciais. Para avaliar os efeitos do envelhecimento hidrotermal nas propriedades mecânicas, 270 discos de Y-TZP foram cortados, 90 para cada tipo, sinterizados e atribuídos a 3 grupos: C-Controle; E1- envelhecido até 26h e E2- envelhecido até 140 horas. Os discos foram testados em uma máquina de teste universal (EMIC). A microestrutura dos discos foi avaliada sob MEV. As curvas de cinética do envelhecimento funcionaram de forma semelhante para todas as zircônias utilizadas neste estudo, caracterizadas por uma rápida transformação de fase T-M em função do tempo e estabilização de um platô após uma média de 26 horas. As camadas superficiais apresentam concentrações mais elevadas de fase monoclínica à medida em que essa concentração diminuiu em camadas mais profundas. O envelhecimento hidrotermal através de 140h diminuiu a tenacidade da cerâmica VITA YZ em 17% (681,78 ± 121,18) quando comparado ao seu grupo controle (841,69 ± 56,01), enquanto que as zircônias de alta translucidez não mostraram diferenças estatísticas de resistência flexural após o envelhecimento. O envelhecimento hidrotermal induz a transformação da fase martensítica de fora para dentro do material e não afeta as propriedades mecânicas das cerâmicas VITA HT e INCORIS TZI, enquanto diminui a dureza do material da zircônia VITA YZ. / To evaluate, map and characterize the effects of the accelerated aging kinetics of high translucency zirconias, this study was split into 2 parts: One part evaluating the superficial changes after in vitro hydrothermal aging and the second part aiming the effects of this aging on the mechanical properties of those ceramics. 117 Y-TZP (VITA YZ, VITA HT, InCoris TZI) blocks were cut, 39 for each commercial zirconia, sintered (1530 ºC, 2h) and assigned to 13 groups with 3 samples each: One being a control, aging-free group, and 12 groups that were prematurely aged hydrothermally at 134 ºC and constant pressure of 2 bars through 6, 10, 14, 18, 22, 26, 30, 40, 60, 80, 100 and 140 hours. XRD was used to quantify the amount of zirconia phase transformation (tetragonalmonoclinic) on different depths of the material by swapping the anode tube (Cr, Co, and Cu). An aging kinetic curve was made for each depth for the 3 commercial zirconias. To evaluate the effects of the hydrothermal aging on the mechanical properties, Y-TZP blocks were rounded to a cilindrical shape. 270 discs were cut, 90 for each kind, sintered as mentioned above and assigned to 3 groups: C-Control; E1- Aged through 26h and E2- Aged through 140h. Disks were then tested in a universal testing machine (EMIC) under a load of 1000 kg till fracture of the specimen and the surface was evaluated under SEM. The aging kinetics curves work similarly for all the YTZP used in this study, characterized by phase transformation ascendant and plateau stabilization as far as the aging goes. Superficial layers present higher concentrations of monoclinic phase as it decreases in deeper layers. Hydrothermal aging through 140h decreased VITA YZ toughness by 17% (681,78 ± 121,18) when compared with its control group (841,69 ± 56,01), while high translucency zirconias didn't show any statistical differences after aging.Hydrothermal aging does induce martensitic phase transformation from the outside-to-inside the material and doesn't affect the mechanical properties of VITA HT and INCORIS TZI ceramics, while it decreased the material toughness of VITA YZ zirconia. / FAPESP: 16/03688-1
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/152667 |
| Date | 12 January 2018 |
| Creators | Prado, Pedro Henrique Condé Oliveira |
| Contributors | Universidade Estadual Paulista (UNESP), Marinho, Renata Marques de Melo [UNESP], Campos, Tiago Moreira Bastos |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds