Experimental work evaluated the dependence of the thickness of the cutting edge, its roughness and assessment of appearance with regard to the defects resulting from the diameter of the focal spot during oxidative cutting Yb:YAG laser. Other variables include the experiment: process parameters such as laser power, cutting speed, oxygen pressure and focus position. Experiment is based on the Taguchi tables. Test samples were cut off from sheet thickness 10, 15 and 20 mm. Representatives of conventional steel were S235JRC+N, S235JR, S235JR+N and steel type RAEX developed for laser and plasma cutting. Samples were evaluated according to the ČSN EN ISO 9013. The evaluation of samples was into classes according to standards of quality. Hardness measurements were performed on the samples thickness 20 mm of convectional steel and steel type RAEX.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:241916 |
| Date | January 2016 |
| Creators | Maňas, Petr |
| Contributors | Kaván, Martin, Mrňa, Libor |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds