Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2017. / Made available in DSpace on 2017-10-31T03:18:34Z (GMT). No. of bitstreams: 1
348411.pdf: 4802564 bytes, checksum: 9cc094244049a235efb2cb367ac0e889 (MD5)
Previous issue date: 2017 / Laminados cerâmicos começaram a ser produzidos de forma que interfaces, camadas ou tensões residuais térmicas fossem utilizadas com intuito de se oporem ao início do crescimento de trinca e/ou poderem desenvolver uma resistência limite que deveria ser ultrapassada para que houvesse tal crescimento. O presente estudo teve como objetivo produzir compósitos particulados de alumina tenacificada com zircônia (ZTA, zirconia-toughened alumina), nos quais a zircônia empregada é parcialmente estabilizada com ítria (Y-PSZ, yttria-partially stabilized zirconia), dotados ou não de camadas intermediárias de Y-PSZ como fase de reforço. O trabalho foi dividido em duas partes. A primeira parte visou desenvolver ZTAs sinterizados com 5 vol% e 30 vol% de Y-PSZ processados via colagem de fitas (tape casting) e caracterizá-los microestrutural e mecanicamente. A segunda parte do trabalho teve como objetivo produzir compósitos laminados sinterizados com camadas de ZTA (os mesmos da primeira parte) alternadas com camadas de Y-PSZ produzidas por tape casting e centrifugação (spin coating), caracterizando sua microestrutura e comportamento mecânico. Os resultados mostraram que a adição de Y-PSZ em 5 vol% na matriz de alumina refinou os grãos de Al2O3, trazendo um consequente aumento da resistência média à flexão de 284,7 MPa para 340,0 MPa. Entretanto, a tenacidade à fratura não variou. A adição de Y-PSZ em 30 vol% resultou numa microestrutura com tamanho médio de grão de alumina ainda menor, com formação de núcleos de zircônia que permitiram a ela ativar seus mecanismos de tenacificação e, dessa forma, aumentar a resistência média à flexão em ~20% e a tenacidade à fratura de 3,0 MPa·m½ para 4,2 MPa·m½ comparados ao ZTA com 5 vol% de Y-PSZ. As fases de reforço produzidas via tape casting e spin coating aumentaram a resistência média à flexão em ~21% e ~43% respectivamente. Compósitos laminados com camada espessa de ZTA com 30 vol% de Y-PSZ e com camada fina processada por spin coating apresentaram maiores valores resistência mecânica média (361,7 MPa) e confiabilidade (m = 9,8). O comportamento mecânico dos compósitos se mostrou dependente da microestrutura, dos mecanismos de tenacificação e das tensões residuais térmicas impostas durante o resfriamento após a sinterização.<br> / Abstract : Ceramic laminates began to be produced in such a way that interfaces, layers or thermal residual stresses were used in order to oppose the beginning of crack growth and/or to develop a threshold strength that should be exceeded in order to achieve such growth. The aim of the present study was to produce particulate composites of zirconia-toughened alumina (ZTA), in which zirconia was partially stabilized with yttria (Y-PSZ) with or without intermediate Y-PSZ layers as reinforcement phase. The work was divided into two parts. The first part aimed to develop sintered ZTAs with 5 and 30 vol% Y-PSZ processed through tape casting and to characterize them microstructurally and mechanically. The second part of the work had as objective to produce sintered laminated composites with layers of ZTA (the same of the first part) alternated with layers of Y-PSZ produced by tape casting and spin coating, characterizing its microstructure and mechanical behaviour. The results showed that the addition of 5 vol% Y-PSZ in the alumina matrix refined the Al2O3 grains, bringing a consequent increase in mean flexural strength from 284.7 MPa to 340.0 MPa. However, fracture toughness did not change. The addition of Y-PSZ in 30 vol% resulted in a microstructure with an even smaller alumina grain size, with formation of zirconia clusters that enabled it to activate its toughening mechanisms and, thus, increase the mean flexural strength in ~20% and fracture toughness from 3.0 MPa·m½ to 4.2 MPa·m½ compared to ZTA with 5 vol% Y-PSZ. The reinforcement phases produced by tape casting and spin coating increased the mean flexural strength in ~21% and ~43% respectively, compared to ZTA without reinforcement layer. Laminated composites with thick ZTA layer with 30 vol% of Y-PSZ and thin layer processed by spin coating presented the highest value of mean flexural strength (361.7 MPa) and reliability (m = 9,8). The mechanical behaviour of the composites was shown to be dependent on the microstructure, the toughening mechanisms and thermal residual stress imposed during the cooling.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/180551
Date January 2017
CreatorsBarros, Marcelo Daniel
ContributorsUniversidade Federal de Santa Catarina, Hotza, Dachamir, Rachadel, Priscila Lemes
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format127 p.| il., gráfs., tabs.
Sourcereponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds