The aim with this master thesis was to investigate the potential of using non-wood fibers to enhance the paper strength. Abaca, sisal and banana fibers were added to conventional bleached chemical softwood pulp. The effect of refining was investigated, both as co-refining and as separate refining. The fiber properties were determined with a Fiber Tester and the drainage resistance was determined with Schopper-Riegler. Density, tensile index, tear index and burst index were determined on paper sheets made in a Rapid-Köthen sheet former. The results showed that abaca had longer fiber length than softwood, while sisal had slightly shorter fiber length compared with softwood. Sheet density was lowered with addition of all three fiber types, while the drainage resistance was increased for the same. It was also observed that the tensile index increased with additions of abaca, while additions of sisal and banana fibers gave lower tensile indexes. The same trend was observed for the tear index and burst index. Refining gave higher values of the drainage resistance, density, tensile index and burst index. However, the tear index was affected differently depending on the fiber type and fiber blend. For sisal and banana fibers, the tear index was first increased at lower refining degrees and were thereafter decreased with further refining. When studying abaca and softwood, a declining trend was observed over the entire refining interval. The conclusion was that addition of abaca fibers increased all investigated strength properties. Sisal and banana fibers gave higher values of the tear strength, when exposed to mild refining.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kau-78679 |
| Date | January 2020 |
| Creators | Rinaldo, Emilia |
| Publisher | Karlstads universitet, Institutionen för ingenjörs- och kemivetenskaper (from 2013) |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds