Orientador: Lourenço Correr Sobrinho, Lucas Zago Naves / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T09:40:26Z (GMT). No. of bitstreams: 1
Soares_EvelineFreitas_M.pdf: 1985707 bytes, checksum: 7527104238577fafc96b875141e96321 (MD5)
Previous issue date: 2013 / Resumo: O propósito deste estudo in vitro foi a avaliar a ação da radiação na interface de união dente humano-compósito fotoativado, através do ensaio de resistência de união à microtração (?TBS) variando: dois sistemas adesivos, com ou sem aplicação da Doxiciclina, com ou sem radiação e análise do padrão de fratura. A superfície oclusal de sessenta terceiros molares humanos foi desgastada com lixa de carbeto de silício de granulação 600. Os dentes foram divididos em 3 grupos (n=20) de acordo com o sistema adesivo (Adper Scotchbond MP e Clearfil SE Bond), com ou sem aplicação da Doxiciclina e submetidos ou não a radiação com 60 Gy, fracionados em doses diárias de 2Gy durante 5 dias por semana, num período de 6 semanas. Grupo Controle (n=20) não recebeu radioterapia; Grupo IrrRe (n=20) submetido à radioterapia antes de ser restaurado; e, Grupo ReIrr (n=20) submetido à radioterapia após ser restaurado. Um bloco de resina Z250 (3M ESPE) com 5 mm de espessura foi construído sobre a dentina com os sistemas adesivos, preparados de acordo com as recomendações do fabricante e cada camada de 2 mm de espessura foi fotoativada por 40 segundos com o aparelho UltraLume 5 (Ultradent). Após 24 horas à 37º C, as amostras foram seccionadas perpendicularmente à área de união, para obter palitos com área de secção transversal de 1mm2. Em seguida, os palitos foram submetidos ao ensaio de resistência de união à microtração em máquina de ensaio universal (EZ-Test) a velocidade de 0,5 mm/minuto. A análise do modo de falha foi observada em lupa estereoscópica (Leica Mz 9.5). Os dados foram submetidos à Análise de Variância com 3 fatores e ao teste de Tukey (5%) e mostram que nenhuma diferença estatística foi observada entre os sistemas adesivos. O uso do antimicrobiano Doxiciclina reduziu significativamente a resistência de união, quaisquer que fossem as demais condições. A radiação das amostras antes do procedimento da restauração em compósito reduziu significativamente a resistência de união à microtração. O modo de falha coesiva na dentina foi predominante nas amostras submetidas à radiação antes do procedimento restaurador, e mistas nas amostras restauradas e submetidas à radiação. Falhas mistas e adesivas foram observadas no grupo controle / Abstract: The purpose of this in vitro study is to evaluate radiation effect on human interface bonding to dentin- light cured composite, using microtensile bond strength test (?TBS) ranging: two adhesive systems, with or without Doxycycline application; with or without radiation submission, and the analysis of mode of failure. Flat occlusal dentin of sixty third human molars was exposed using wet ground with 600-grit SiC paper. The teeth were distributed into 3 groups (n=20) according to adhesive systems (Adper Scotchbond MP and Clearfil SE Bond), with or without application of Doxycycline and submitted or not to 60 Gy radiation, in 2 Gy daily fractionated doses during 5 days per week in a total of 6 weeks. Control group (n=20) did not go throw radiotherapy; Group IrrRe (n=20), submitted to radiotherapy before the restoration procedure; Group ReIrr (n=20) submitted to (IrrRe; n=20) submitted to radiotherapy after the restoration procedure. A block of 5mm thickness resin composite Z250 (3M ESPE) was constructed on dentin using adhesive systems according to manufacturer's instructions and each 2mm thickness was light cured for 40 seconds using a light curing unit UltraLume 5 (Ultradent). After 24 h storage at 37oC in deionized water, the specimens were sectioned perpendicularly to bond area to obtain beams in a sectional area of 1 mm2. After that, the beams were submitted to microtensile bond strength (?TBS) test in a universal test machine (EZ-Test) at a crosshead speed of 0.5mm/min. The mode of failure analyses was observed under optical microscopy (Leica Mz 9.5). Data were submitted to two-way ANOVA, Tukey's test (p<0.05) and showed that no statistical difference was observed between the adhesive systems. The use of antimicrobial Doxycycline decreased significantly bond strength, whatever other conditions. The specimens submitted to radiation before restoration procedure decreased significantly microtensile bond strength. Dentin cohesive failure mode was predominantly for specimens submitted to radiation before restoration procedure, and mixed failure mode for specimens restored then submitted to radiation. Mixed and adhesive failures were observed in control group / Mestrado / Materiais Dentarios / Mestra em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289603 |
| Date | 22 August 2018 |
| Creators | Soares, Eveline Freitas, 1987- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Naves, Lucas Zago, 1981-, Correr Sobrinho, Lourenço, 1960-, Sinhoreti, Mário Alexandre Coelho, Sunfeld, Renato Herman |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 81 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds