To evaluate potential uses for friction stir welding in additive manufacturing, two separate parts were fabricated, one of 2195-T84 and the other 2219-T87, utilizing fixed pin techniques and additive lap welds. The parts were cut into samples, artificially aged and subjected to Rockwell hardness (HRB), Vickers hardness, micrographic photography, and metallographic imaging on both pre- and post- heat treatment. Additionally, tensile testing was performed on the heat-treated samples. A comparisons of test results showed a minimal increase in the yield strength of the 2195-T84 samples compared to as-welded tensile results obtained from a previous project. The ultimate tensile strength was reduced by approximately 16%. Further testing will be required to determine the nature of this reduction. No previous results were available for the as-welded 2219-T87, but UTS of the artificially aged samples was approximately 91% that of the parent material.
| Identifer | oai:union.ndltd.org:uno.edu/oai:scholarworks.uno.edu:td-3556 |
| Date | 20 December 2017 |
| Creators | Champagne, Matthew |
| Publisher | ScholarWorks@UNO |
| Source Sets | University of New Orleans |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | University of New Orleans Theses and Dissertations |
Page generated in 0.0019 seconds