Multilayer structures of AlxIn1-xAsySb1-y/GaSb (0.37 £ x £ 0.43, 0.50 £ y £ 0.52), grown by molecular beam epitaxy on GaSb (100) substrates were characterized using variable temperature Hall and Shubnikov-de Haas techniques. For nominally undoped structures both p and n-type conductivity was observed. The mobilities obtained were lower than those predicted by an interpolation method using the binary alloys; therefore, a detailed analysis of mobility versus temperature data was performed to extract the appropriate scattering mechanisms. For p-type samples, the dominant mechanism was ionized impurity scattering at low temperatures and polar optical phonon scattering at higher temperatures. For n-type samples, ionized impurity scattering was predominant at low temperatures, and electron-hole scattering dominated for both the intermediate and high temperature range. Analyses of the Shubnikov-de Haas data indicate the presence of 2-D carrier confinement consistent with energy subbands in GaAszSb1-z potential wells. Epilayers of GaAs1-xSbx (0.19<x<0.71), grown by MBE on semi-insulating GaAs with various substrate orientations, were studied by absorption measurements over the temperature range of 4-300 K. The various substrate orientations were chosen to induce different degrees of spontaneous atomic ordering. The temperature dependence of the energy gap (Eg) for each of these samples was modeled using three semi-empirical relationships. The resulting coefficients for each model describe not only the temperature dependence of Eg for each of the alloy compositions investigated, but also for all published results for this alloy system. The effect of ordering in these samples was manifested by a deviation of the value of Eg from the value of the random alloy. The presence of CuPt-B type atomic ordering was verified by transmission electron diffraction measurements, and the order parameter was estimated for all the samples investigated and found to be larger for the samples grown on the (111) A offcut orientations. This result strongly suggests that it is the A steps that contribute to the formation of the CuPt-B type ordering in the GaAs1-xSbx alloy system.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc5522 |
| Date | 05 1900 |
| Creators | Lukic- Zrnic, Reiko |
| Contributors | Littler, Chris, Golding, Terry, Duggan, Jerome L., Weathers, Duncan L. |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Copyright, Lukic- Zrnic, Reiko, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0012 seconds