Ferroelectric ceramics are very promising materials for a variety of piezoelectric applications such as high permittivity dielectrics, piezoelectric sensors, piezoelectric/electrostrictive transducers, actuators, electro-optic devices, etc. Among the commercially viable ferroelectric ceramics, the lead-zircon ate-titivate Pb(Zr1-xTix)O3 (PZT) based ceramics have dominated the market due to their superior piezoelectric and dielectric property along with other advantages like high electromechanical coupling, ease of processing and low cost. However, the toxicity of lead based materials, and its volatility at processing temperatures is a serious health and environmental concern. Several legislations against lead-based products have been passed all over the world in order to encourage identification of alternative lead-free materials for these applications. As a consequence, there has been a remarkable surge in efforts by researchers on identifying lead-free alternatives for piezoelectric applications. A larger emphasis has been placed on perovskite based ceramics since in addition to possessing excellent properties, their relatively simple structure facilitates understanding structure-property relationships which are important for developing novel high performance materials. Na1/2Bi1/2TiO3 (NBT) and its solid solutions are one of the leading classes of perovskite ceramics, which show promising ferroelectric, piezoelectric and dielectric property thereby having the potential to replace PZT based ferroelectrics. The parent compound NBT is ferroelectric with large ferroelectric polarization (~40 C/cm2), promising piezoelectric properties with 0.08% maximum strain and longitudinal piezoelectric coefficient (d33) ~ 80 pC/N.
Though NBT was discovered nearly six decades ago, a clear understanding of its structure remained elusive for a long time since different characterization techniques yielded contradicting reports on its structure and nature of phase transformation. However, rapid advances in characterization techniques in recent years have led to uncovering of new results, thereby shedding light on the true structure of NBT. X-ray and neutron diffraction studies in the past have shown that NBT exhibits rhombohedral (R3c) structure at room temperature, which
undergoes a gradual transformation into tetragonal (P4bm) structure at ~230oC. However, recent characterization of both single crystal and powder of NBT using high resolution x-ray diffraction showed that the room temperature structure is not purely rhombohedral and the structure can be better modeled with a monoclinic (Cc) structure. In contrast to x-ray and neutron diffraction,
electron diffraction studies have shown evidence for the presence of planar disorders, corresponding to in-phase octahedral tilts in the sample which cannot be accounted for by either R3c or Cc structure. In addition, EXAFS, x-ray and neutron total scattering studies, diffuse scattering studies, etc. have shown that the structural parameters obtained from bulk diffraction techniques are significantly different from the local structure of the material. Similar ambiguities have been observed even in NBT based solid solutions like BaTiO3, K1/2Bi1/2TiO3, etc. which show enhanced properties at the morphotropic phase boundary (MPB).
A major breakthrough in understanding the structural complexity involved in NBT based solid solutions was achieved when it was found that the structure of the MPB compositions were sensitive to electric field. This led to solving the mystery behind the appearance of cubic-like phase at some of the MPB compositions where the application of electric-field resulted in the transformation of the structure into a co-existence of rhombohedral and tetragonal phases. Observation of an electric-field-induced structural transition at the MPB compositions was expected, because the MPB signifies instability in the system and even a minor external force can significantly influence the system. However, we have found that the structure of even pure NBT is significantly influenced by electric field and the framework of this thesis is based on this particularly important result. The intrinsic tendency of the electric field to affect the structure of NBT is a major factor which needs to be considered when studying similar phase transitions in the MPB compositions of NBT-substituted systems also. This was not taken into account by other research groups, and they assumed that the instability associated with the MPB was the only major factor involved in the electric-field induced transitions. A simple but highly effective strategy of grinding the electrically poled pellet into fine powder and then collecting x-ray diffraction patterns, facilitated elimination of preferred orientation in the sample. Thus, structural analysis by Rietveld refinement was possible even on the poled sample, which has not been carried out by any other groups on any ferroelectric ceramics so far. The initial part of the thesis deals with addressing the structural complexity of pure NBT, wherein the effect of electric field on the bulk structure as well as the local structure was studied in great detail. Later on, similar concepts are used to investigate BaTiO3 and K1/2Bi1/2TiO3 substituted NBT also.
The first chapter of the thesis provides a brief introduction to the field of ferroelectrics, perovskite structure and their phase transition. An exposure to concepts like relaxor ferroelectrics, morphotrophic phase boundary, octahedral tilting, etc. has been provided. Then, a
detailed overview of the existing literature related to the structure of NBT and its phase transition studies with temperature has been discussed. The details of the experimental procedures, characterization techniques used, and some theory behind these techniques have been provided in chapter 2.
The third chapter deals with the room temperature structural characterization of pure NBT using techniques like x-ray diffraction, neutron diffraction, electron diffraction and EXAFS analysis. The results of these structural characterizations are also complemented with first-principles calculation study of the ground state structure of NBT, dielectric and ferroelectric characterization, and ageing studies. While x-ray and neutron diffraction clearly established electric-field induced structural transition from a monoclinic (Cc) to rhombohedral (R3c) structural transition, first principles calculation showed that the monoclinic phase is not stable and hence cannot be the ground state structure of NBT. Also, the possibility of the monoclinic features appearing in the x-ray diffraction solely due to micro structural effects by nano-sized domains was discussed. Comparison of electron diffraction of poled and unpoled samples of NBT showed that the in-phase tilted regions were greatly suppressed in the poled samples. Even HRTEM images showed that the unpoled samples had a very high concentration of strain heterogeneity in them, which was absent in the poled samples. This gave a direct evidence of correlation between observation of monoclinic phase and the presence of in-phase tilted regions in the unpoled samples. It was proposed that the strain caused by these in-phase tilted disorders caused distortion in the original rhombohedral lattice thereby making the structure appear monoclinic. Application of electric field causes the in-phase octahedral tilt disorders to vanish, thereby even the monoclinic features observed in the XRD also disappear.
The fourth chapter discusses the consequences of poling on the high temperature phase transition behavior of NBT. We have used temperature dependent x-ray and neutron diffraction, Raman spectroscopy and EXAFS analysis whose results were correlated with the anomalies observed in temperature dependent dielectric and polarization studies. We found that the poled sample shows a sharp anomaly at the depolarization temperature (Td) in all the characterization techniques used, in contrast to a diffuse or negligible effect seen in the unpoled sample. The depolarization temperature was found to be associated with introduction of structural disorder in the sample in the form of in-phase octahedral tilts. This also gave rise to a normal to relaxor ferroelectric transition at Td, and this relaxor behavior persisted even after cooling the sample to
room temperature. An intermediate cubiclike phase was observed from x-ray diffraction at around 300C wherein the rhombohedral phase vanishes and the tetragonal phase begins to appear. Even single crystal study of NBT in the past showed sudden disappearance of the domains at 300C, even though they were visible at both above and below this temperature. This effect was called isotropization, and was postulated to arise due to extremely small domains which made the system isotropic. However, our neutron diffraction pattern showed that in-phase tilted superlattice reflections persisted at this temperature which meant that the structure was not truly cubic at this temperature. Further, a neutron diffraction study at higher temperatures showed that the in-phase tilted superlattice reflections persisted even above the cubic phase transition temperature, in corroboration with similar reports from high temperature electron diffraction.
Chapter five deals with the BaTiO3 substituted NBT system, which has gained tremendous interest in the last decade as a viable piezoelectric ceramic for commercial applications. Though a large number of groups have already carried out exhaustive studies on this system, most of the work concentrated mainly on the MPB compositions which showed enhanced piezoelectric properties. In this chapter, we highlight some important findings in the pre-MPB and post-MPB compositions. Using room-temperature and high temperature x-ray diffraction, we show that there exists a subtle compositional phase boundary at x = 0.03, which disappears upon poling the sample. While the monoclinic phase in pure NBT becomes cubiclike at this composition, the depolarization temperature (Td) also slightly increases up to this composition and then decreases upon further Ba substitution. Similar studies were also carried out with compositions containing slightly excess bismuth in them (0.1 mol %), whose purpose was to negate the effects of Bi-vaporization during sintering. It was found that while the compositional phase boundary remained essentially unchanged, there was a decrease in Td for all the compositions. It was also realized that the addition of excess bismuth improved the overall piezoelectric property of the system.
Studies on higher compositions of Ba in the post-MPB regions further revealed two additional compositional phase boundaries. A criticality in the coercive field and spontaneous tetragonal strain was observed at x = 0.2, which was found to be associated with crossover from a long-period modulated tetragonal phase (for x < 0.2) to a no modulated tetragonal phase (for x > 0.2). Near the BT rich end (x ~ 0.7), the system exhibits a crossover from normal to a
diffuse/relaxor ferroelectric transition with increasing Na1/2Bi1/2 substitution. The onset of relaxor state by Na1/2Bi1/2 substitution on the Ba-site, was shown to increase the spontaneous tetragonal strain in the system. This was because of the enhancement in the covalent character of the A-O bond by virtue of the Bi+3 6s2 lone pair effect, and it also led to a sudden increase in the tetragonal-to-cubic transition temperature. This was in contrast to other chemical modifications of BT reported in the past (like Zr, Sn, Sr, etc.) where the relaxor state is accompanied by a weakening of the ferroelectric distortion and a decrease in the critical temperature.
Finally, chapter six covers the effect of electric field induced phase transition in K1/2Bi1/2TiO3 substituted NBT. Visual observation showed that while the compositions (x < 0.2) behaved similar to pure NBT, wherein the structure became purely rhombohedral upon poling, the effect of electric field was negligible in the post-MPB compositions (x > 0.2). In addition, the peaks in the annealed samples were considerably overlapping which made identifying the structural transitions at the MPB compositions difficult using Rietveld analysis. However, comparison of the FWHM of the {200}pc peaks of compositions x < 0.2 showed that the FWHM began to increase suddenly for x > 0.15 indicating emergence of the tetragonal phase. Also, all the compositions showed an increase in the {200}pc peak FWHM by 0.03 after poling. The depolarization temperature showed only slight variation in the pre-MPB compositions, but showed a minimum at the MPB compositions. Temperature dependent dielectric studies further showed that for the post-MPB compositions, the system remains relaxor even after poling.
Identifer | oai:union.ndltd.org:IISc/oai:etd.iisc.ernet.in:2005/3966 |
Date | January 2015 |
Creators | Badari Narayana, A R |
Contributors | Ranjan, Rajeev |
Source Sets | India Institute of Science |
Language | en_US |
Detected Language | English |
Type | Thesis |
Relation | G27271 |
Page generated in 0.0022 seconds