Obtenção e caracterização de compósitos de blendas poliméricas biodegradáveis reforçadas com bio-hidroxiapatita / Obtaining and characterization of composites based on biodegradable polymeric blends reinforced with bio-hydroxyapatite

Este trabalho apresenta a preparação e caracterização de materiais compósitos baseados na mistura (blenda) de poli (ácido lático) PLA e poli (adipato co-tereftalato de butileno) PBAT reforçados com bio-hidroxiapatita \"HAp\", obtida a partir de cascas de ovos brancos de galinha. A obtenção de HAp foi realizada por via úmida, reação ácido-base. Primeiramente, foi obtido o bio-carbonato de cálcio a partir das cascas de ovos brancos de galinha, seguido de um ciclo térmico de aquecimento a 800 °C para a conversão em óxido de cálcio, o qual posteriormente foi sinterizado a 900 °C para a obtenção da HAp. Os materiais compósitos de PLA/PBAT reforçados com 1, 3 e 5 %, em massa, de HAp em pó, com tamanho de partículas iguais ou menor que 10 μm, foram preparadas pelo processo de extrusão utilizando-se uma extrusora de dupla-rosca. Após o processo de extrusão, os materiais foram alimentados ao funil de alimentação de uma injetora de laboratório para a obtenção dos corpos de prova para os ensaios de caracterização. Parte dos corpos de prova foram submetidos à esterilização por radiação gama (radioesterilização), utilizando-se feixe de elétrons de alta energia, gerados em um acelerador de elétrons industrial, de 1,5 MeV, à temperatura ambiente e na presença de ar, com dose de radiação de 25 kGy. As amostras de HAp foram caracterizadas por meio dos ensaios de difração de raios X (DRX), espectroscopia vibracional de absorção no infravermelho com transformada de Fourier (FTIR), termogravimetria (TG) e microscopia eletrônica de varredura com fonte de emissão de campo (MEV-FEG). O PLA/PBAT puro e seus compósitos não irradiados e irradiados foram caracterizados por meio dos ensaios de DRX, TG, MEV-FEG, calorimetria exploratória diferencial (DSC), temperatura de distorção térmica (HDT), ponto de amolecimento Vicat, resistência à tração, à flexão e ao impacto Izod, validação do processo de esterilização (teste de carga microbiana (Biocarga ou Bioburden) e ensaios de esterilidade) e citotoxicidade \"in vitro\" pelo método de incorporação do vermelho neutro para avaliação da biocompatibilidade das amostras. As análises de DRX da HAp mostraram os picos característicos presentes na fase amorfa da HAp; os picos e bandas largas pertencentes aos grupos moleculares da HAp foram identificados por meio da análise por FTIR; a estabilidade térmica da HAp obtida foi confirmada por termogravimetria, a qual mostrou uma pequena perda de massa com o aumento da temperatura, devido à queima do solvente, evaporação de água e queima de materiais orgânicos presentes na amostra de HAp, as imagens obtidas por MEV-FEG mostraram estruturas irregulares características da HAp. A incorporação de HAp na blenda de PLA/PBAT promoveu ganhos superiores a 10 % na temperatura de distorção térmica e no ponto de amolecimento Vicat original da blenda, aumento superior a 15 % nas propriedades mecânicas de resistência à tração e à flexão, e aumento superior a 10 % a resistência ao impacto Izod, melhorando suas propriedades de forma significativa quando comparado a blenda de PLA/PBAT. Os testes de carga microbiana e esterilidade mostraram que a dose de radiação de 25 kGy aplicada foi eficaz para a esterilização das amostras dos materiais. Todas as amostras apresentaram-se biocompatíveis em ambiente celular pelo teste de citotoxicidade \"in vitro\", apresentando potencial para estudo \"in vivo\". / This work presents the preparation and characterization of composites based on blends of poly (lactic acid) - PLA and poly (adipate co-terephthalate of butylene) - PBAT reinforced with bio-hydroxyapatite \"HAp\", obtained from avian eggshells waste of white color. The HAp was obtained by the wet chemical method from the acid-base reaction. Firstly, the bio-calcium carbonate (bio-CaCO3) was obtained from the avian eggshells waste. The bio-CaCO3 was submitted to a heating cycle at 800 °C in order to convert bio-CaCO3 in the bio-calcium oxide, which was then sintered at 900 °C and the bio-HAp was obtained. PLA/PBAT reinforced with 1, 3 and 5 % in weight of HAp, particle size ≤ 10 μm, were prepared by the extrusion process using a twin-screw extruder. After the extrusion process, the PLA/PBAT blend and its composites were fed into a laboratory injection molding machine and the specimens test were obtained for the characterization tests. Part of the specimens was submitted to sterilization by gamma radiation (radio-sterilization) with electron-beam using an industrial electron accelerator of 1.5 MeV, at the radiation dose of 25 kGy, room temperature and in the presence of air. HAp was characterized by X ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), thermogravimetry (TG) and scanning electron microscopy with field emission source (FE-SEM) analysis. The blends and composites (non-irradiated and irradiated samples) were characterized by XRD; TG; FE-SEM and differential scanning calorimetry (DSC) analysis. The thermal distortion temperature (HDT), Vicat softening temperature, tensile, flexural, and impact Izod tests were also carried out. The validation of materials sterilization process (Bioburden tests) and cytotoxicity test \"in vitro\" to evaluating the biocompatibility of the material composites were also made. XRD analyzes results showed a characteristic peak in the amorphous phase of HAp. FTIR analysis identified broad peaks and bands belonging to the molecular groups of HAp. The thermal stability of the HAp was confirmed by the TG analysis, which showed a small loss of mass with the increase of temperature due to the burning of solvents, water evaporation and burning of organic materials present in the sample of HAp. The FE-SEM images showed irregular structures characteristic of HAp. Regarding the PLA/PBAT/HAP composites, it can be observed increases up to 10 % in thermal distortion temperature and Vicat softening temperature, higher than 15 % in the tensile and flexural strength, and higher than 10 % in the Izod impact when compared with neat PLA/PBAT blend. The bioburden tests showed that radiation dose of 25 kGy was effective for sterilization of the materials. The results of the cytotoxicity test \"in vitro\" showed that all samples are biocompatible in the cellular environment, and therefore, presents a potential for \"in vivo\" study.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-01112018-151923
Date03 October 2018
CreatorsPedro Rodrigo de Sousa Reis
ContributorsEsperidiana Augusta Barretos de Moura, Fábio José Esper, Derval dos Santos Rosa
PublisherUniversidade de São Paulo, Tecnologia Nuclear, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds