Eletrofiação de nanofibras de blendas de gelatina/PVP (poli (vinil pirrolidona)) a partir de soluções de água e ácido acético / Electrospinning of nanofibers of gelatin/PVP (poly (vini pyrrolidone)) blends from water/acetic acid solutions

Orientador: Marcos Akira d'Ávila / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-22T03:44:39Z (GMT). No. of bitstreams: 1
Salles_TaisHelenaCosta_M.pdf: 2536678 bytes, checksum: 358cfaf694adc91a715f58aabead529d (MD5)
Previous issue date: 2013 / Resumo: A eletrofiação é reconhecida como uma técnica eficiente para a fabricação de microfibras e nanofibras de polímero, devido à sua versatilidade e potencial para aplicações em diversos campos. As aplicações notáveis incluem engenharia tecidual, biossensores, filtração, curativos, liberação controlada de fármacos e imobilização de enzimas. As nanofibras são geradas através da aplicação de um campo elétrico em uma solução polimérica. As fibras fiadas por este processo oferecem várias vantagens, como elevada área de superfície em relação ao volume, alta porosidade e a capacidade de manipular a composição de nanofibras, a fim de obter as propriedades e funções desejadas. Neste trabalho, a eletrofiação de blendas de gelatina com polivinilpirrolidona (PVP) para a fabricação de nanofibras foi investigada. Os polímeros foram fiados a partir de soluções contendo diversas concentrações de água e ácido acético. As soluções foram fiadas a uma tensão positiva de 29,0-29,2 kV, uma distância da ponta da agulha ao coletor de 10 cm, e uma vazão de 1 mL / h. Todas as soluções foram avaliadas quanto ao pH, condutividade elétrica, tensão superficial e viscosidade. Foram investigados os efeitos da concentração de ácido acético nas propriedades das soluções que por sua vez, influenciaram no processo de obtenção de fibras por eletrofiação. Foi observado que há uma correlação entre a concentração de ácido acético e a formação de fibras desse sistema, assim como a influência no diâmetro final das fibras. No presente estudo, uma matriz de nanofibras uniformes com diâmetro aproximado de 519, 355 e 154 nm foram produzidas via eletrofiação. A morfologia das membranas foi avaliada por Microscopia Eletrônica de Varredura (MEV). Foi realizada a análise térmica termogravimétrica (TGA) e avaliação de citotoxicidade, visando futuras aplicações em engenharia tecidual / Abstract: The electrospinning is recognized as an efficient technique for the fabrication of polymeric microfibers and nanofibers due to its versatility and potential for applications in many fields. Notable applications include tissue engineering, biosensors, filtration, wound dressings, controlled drug release and enzyme immobilization. The nanofibers are generated by applying an electric field in a polymer solution. The fibers spun by this process offers several advantages such as high surface area relative to volume, high porosity and the ability to manipulate the composition of nanofibers in order to obtain the desired properties and functions desired. In this work, the electrospinning blends of gelatin with polyvinylpyrrolidone (PVP) to fabrication nanofibers were investigated. The polymers were electrospun from solutions containing various concentrations of water and acetic acid. The solutions were electrospun at a positive voltage of 29.0 to 29.2 kV, a distance from the needle tip to the collector of 10 cm and a flow rate of 1 mL / h. All solutions were analyzed as your pH, electrical conductivity, surface tension and viscosity. We investigated the effects of acetic acid concentration on the properties of the solutions, on the other hand, influenced the process of obtaining fibers by electrospinning. It was observed that there was a correlation between the concentration of acetic acid and formation of fibers of that system, as well the influence on the final diameter of the fibers. In the present study, a matrix of nanofibers uniform with diameters of approximately 519, 355 and 154 nm had been produced by electrospinning. The morphology of the membranes was evaluated by Scanning Electron Microscopy (SEM). We made thermal analysis (TGA) and assessment of cytotoxicity, aiming future applications in tissue engineering / Mestrado / Materiais e Processos de Fabricação / Mestra em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263536
Date22 August 2018
CreatorsSalles, Taís Helena Costa, 1986-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, D'Avila, Marcos Akira, 1972-, Zavaglia, Cecília Amélia de Carvalho, Lombello, Christiane Bertachini
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format66 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds