This work has as main objective to analyze the mechanical behavior of prisms run
with ceramic bricks and filled with mortar or grout, checking their influence when
subjected to centric compression. An experimental program consists of four different
types of prisms was developed. They were used for making the prisms blocks of
three different Manufacturers. The ceramics were randomly named as Manufacturer
1 Manufacturer 2 and Manufacturer 3, manufacturers have provided the following
resistance of structural blocks: Manufacturer 1 - fbk (A) 6 MPa, Manufacturer 2 - fbk
(E) 7 MPa and fbk (C) 15 MPa Manufacturer 3 - FBK (B) and 6 MPa FBK (D) 15
MPa.The prisms were molded with industrialized mortar. Each prism type with its
respective resistors blocks were molded as follows: hollow prism, prisms filled with
grout (the larger castings), the same used in the settlement, and prisms filled with
grout, totaling 320 prisms, which were subjected to tests to simple axial compression.
The results were analyzed statistically by the Tukey test at 5% significance level. It
was concluded that the grout used not added significant increase in resistance to the
prisms, the study can not say whether it is possible or not to replace the grout by
mortar, to fill the cast, as well as adequate strength of the mortar used in filling It
should be further studied. / Este trabalho tem como objetivo principal analisar o comportamento mecânico de
prismas executados com blocos cerâmicos e preenchidos com argamassa ou
graute, verificando a sua influência quando submetidos à compressão centrada. Foi
desenvolvido um programa experimental composto por quatro diferentes tipos de
prismas. Foram utilizados para confecção dos prismas blocos de três diferentes
cerâmicas. As cerâmicas foram nomeadas aleatoriamente como Fabricante 1,
Fabricante 2 e Fabricante 3. Os fabricantes forneceram as seguintes resistências de
Blocos Estruturais: Fabricante 1 fbk(A) 6 MPa, Fabricante 2 fbk(E) 7 MPa e fbk(C) 15
MPa, Fabricante 3 fbk(B) 6 MPa e fbk(D) 15 MPa. Os prismas foram moldados com
argamassa industrializada. Cada tipo de prisma, com suas respectivas resistências
de blocos, foi moldado da seguinte forma: prismas ocos, prismas preenchidos com
argamassa (nos vazados maiores), a mesma utilizada no assentamento; e prismas
preenchidos com graute, totalizando 320 prismas, os quais foram submetidos a
ensaios à compressão axial simples.Os resultados foram analisados
estatisticamente através do Teste de Tukey com nível de significância de 5%.
Concluiu-se que o graute utilizado não agregou significativo acréscimo de resistência
aos prismas. Pelo estudo realizado não se pode afirmar se é possível ou não
substituir o graute pela argamassa, no preenchimento dos vazados, assim como a
resistência adequada da argamassa com uso no preenchimento deve ser
novamente estudada.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsm.br:1/7937 |
Date | 10 March 2016 |
Creators | Marco, Carlos Eduardo Giacomini de |
Contributors | Rizzatti, Eduardo, Mohamad, Gihad, Roman, Humberto Ramos, Santos, Flávio Antônio dos |
Publisher | Universidade Federal de Santa Maria, Programa de Pós-Graduação em Engenharia Civil, UFSM, BR, Engenharia Civil |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFSM, instname:Universidade Federal de Santa Maria, instacron:UFSM |
Rights | info:eu-repo/semantics/openAccess |
Relation | 300100000003, 400, 300, 300, 300, 300, 300, 9b66c9f0-2354-4856-aa12-cb188ac6b1fb, d762b927-2ee8-431b-9664-8f92124da8d5, afc48477-ff29-4159-9bbf-d65e66e6f627, 91559f04-e076-496c-9740-15a9822ee6af, 9b638543-f5b0-4f1a-a50d-3f1efdeec796 |
Page generated in 0.1955 seconds