Food waste and fashion pollution are two of the significant global environmental issues throughout the recent past. In this research, it was investigated the feasibility of making a leather-like material from bread waste using biotechnology as the bridging mechanism. The waste bread collected from the supermarkets were used as the substrate to grow filamentous fungi species Rhizopus Delemar and Fusarium Venenatum. Tanning of fungal protein fibres was successfully performed using vegetable tanning, confirmed using FTIR and SEM images. Furthermore, glycerol and a biobased binder treatment was performed for the wet-laid fungal microfibre sheets produced. Overall, three potential materials were able to produce with tensile strengths ranging from 7.74 ± 0.55 MPa to 6.92 ± 0.51 MPa and the elongation% from 16.81 ± 1.61 to 4.82 ± 0.36. The binder treatment enhanced the hydrophobicity even after the glycerol treatment, an added functional advantage for retaining flexibility even after contact with moisture. The fungal functional material produced with bread waste can be tailored successfully into leather substitutes using an environmentally benign procedure.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hb-25522 |
| Date | January 2021 |
| Creators | Wijayarathna, Egodagedara Ralalage Kanishka Bandara |
| Publisher | Högskolan i Borås, Akademin för textil, teknik och ekonomi |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds