Lithium–sulfur batteries are highly attractive energy storage systems, but suffer from structural anode and cathode degradation, capacity fade and fast cell failure (dry out). To address these issues, a carbide-derived carbon (DUT-107) featuring a high surface area (2088 m² g⁻¹), high total pore volume (3.17 cm³ g⁻¹) and hierarchical micro-, meso- and macropore structure is applied as a rigid scaffold for sulfur infiltration. The DUT-107/S cathodes combine excellent mechanical stability and high initial capacities (1098–1208 mA h gs ⁻¹) with high sulfur content (69.7 wt% per total electrode) and loading (2.3–2.9 mgs cm⁻²). Derived from the effect of the electrolyte-to-sulfur ratio on capacity retention and cyclability, conducting salt is substituted by polysulfide additive for reduced polysulfide leakage and capacity stabilization. Moreover, in a full cell model system using a prelithiated hard carbon anode, the performance of DUT-107/S cathodes is demonstrated over 4100 cycles (final capacity of 422 mA h gs ⁻¹), with a very low capacity decay of 0.0118% per cycle. Application of PS additive further boosts the performance (final capacity of 554 mA h gs ⁻¹), although a slightly higher decay of 0.0125% per cycle is observed.
Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:36251 |
Date | 19 December 2019 |
Creators | Thieme, Sören, Brückner, Jan, Meier, Andreas, Bauer, Ingolf, Gruber, Katharina, Kaspar, Jörg, Helmer, Alexandra, Althues, Holger, Schmuck, Martin, Kaskel, Stefan |
Publisher | Royal Society of Chemistry |
Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
Language | English |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, doc-type:article, info:eu-repo/semantics/article, doc-type:Text |
Rights | info:eu-repo/semantics/openAccess |
Relation | 2050-7496, 10.1039/c4ta06748g |
Page generated in 0.0016 seconds