Measurement of the strength development of Cemented Paste Backfill in laboratory cast cylinders does not replicate the in situ strengths of CPB in mine stopes. The mass of CPB in a filled stope is large and temperature rises due to the heat of hydration of the cementing materials, thus accelerating the gain in strength, relative to laboratory specimens stored at ambient temperature. The purpose of this study was to determine the impact on strength development when CPB test cylinders were subjected to a temperature profile mimicking that in a large mass, such as a mine stope. Also, maturity (the integral of time and temperature during hydration of the CPB) was compared to actual strengths, and the maturity – strength concept used in concrete technology was applied. It was found that the strength- maturity relationship was applicable to CPB once the base line or datum temperature was adjusted.
| Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/29534 |
| Date | 23 August 2011 |
| Creators | Mozaffaridana, Mahsa |
| Contributors | Hooton, Robert Douglas, Grabinsky, Murray |
| Source Sets | University of Toronto |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis, Image |
Page generated in 0.0023 seconds