Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T17:46:05Z (GMT). No. of bitstreams: 1
Sicoli_EliseuAugusto_D.pdf: 4658696 bytes, checksum: ce260af08392da02937030d7837080d4 (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar o efeito do condicionamento com ácido hidrofluorídrico ( 5 e 10%) e ciclagem térmica na resistência ao microcisalhamento da interface cimento resinoso RelyX ARC - IPS E.max Press. Foram confeccionadas 20 amostras com cerâmica IPS E.max Press de acordo com a recomendação do fabricante. As amostras foram incluídas em tubos de PVC com resina epóxi e divididas em 4 grupos (n=40). Todas as amostras após o condicionamento ácido por 20 segundos foram silanizadas e a confecção dos corpos-de-prova seguiu o mesmo procedimento padrão para a cimentação com RelyX ARC. Os grupos foram separados em: 1- Cerâmica condicionada com ácido hidrofluorídrico a 10%; 2 - Cerâmica condicionada com ácido hidrofluorídrico a 10% e termociclada com 3000 ciclos; 3 - Cerâmica condicionada com ácido hidrofluorídrico a 5% e 4 -Cerâmica condicionada com ácido hidrofluorídrico a 5% e depois termociclada com 3000 ciclos. Após tratamento da superfície da cerâmica foi realizada aplicação de silano RelyX Ceramic Primer. Matrizes de silicone por adição com quatro perfurações de 1 mm de altura por 1 mm de diâmetro foram posicionadas sobre a cerâmica e preenchidas com o cimento RelyX ARC conforme os grupos citados. A fotoativação foi realizada com o aparelho LED UltraLume 5 com 1100 mW/cm2 de irradiância por 40 segundos. As amostras foram mantidas em 100% de umidade relativa a 37°C por 24 horas e levadas a máquina de ensaios Instron para o teste de microcisalhamento com velocidade de 0,5 mm/minuto. Os resultados em MPa (G1: 35,34±5,03; G2: 21,80±6,39; G3: 33,28±7,57; G4: 19,39±5,06) foram submetidos a análise de variância e as médias ao teste de Tukey (p<0,05). A análise estatística mostrou valor de resistência de união ao microcisalhamento significativamente superior para os grupos 1 e 3 (sem ciclagem térmica). Houve diferença estatisticamente significante em relação à concentração do ácido hidrofluorídrico com menor resistência ao microcisalhamento na concentração 5%. Não houve diferença estatística na interação entre os grupos. A análise do padrão de fratura mostrou predominância de fraturas adesivas em todos os grupos; embora os grupos 1 e 3 apresentassem fraturas do tipo coesiva no cimento em maior porcentagem quando comparados aos grupos 2 e 4. Assim concluiu-se que a ciclagem térmica diminuiu a resistência ao microcisalhamento da união adesiva, independentemente da concentração do ácido hidrofluorídrico e as falhas foram predominantemente adesivas / Abstract: The aim of this study was to evaluate the resistence to microshear bond strength from the bonding of cement ceramic IPS E.max Press with resin cement Rely X ARC under etching surface effect with hydrofluoridric acid in concentrations of 5% and 10%. The problems faced in the groups were also analysed. Twenty samples of ceramic were produced according to the manufacturer recommendation. The samples were included in PVC tubes with epoxi resin and separated in 4 groups (n=40). After the etching with acid for 20 seconds, the samples were silanized and the same cementing procedure was done with Rely X ARC. The groups were separated in: 1- Ceramic conditioned with hydrofluoridric acid in 10%; 2- Ceramic conditioned with hydrofluoridric acid in 10%, thermocycled in 3000 cycles with temperature between 5°C and 55°C and baths of 30s in each temperature; 3- Ceramic conditioned with hydrofluoridric acid in 5% and 4- Ceramic conditioned with hydrofluoridric acid in 10%, thermocycled in 3000 cycles with temperature between 5°C and 55°C and baths of 30s in each temperature. After the ceramic surface etching it was applied silane RelyX Ceramic Primer using microbrush. Silicone rubber matrices with four perfurations, 1 mm of thickness by 1 mm of diameter each, were put on the ceramic and fulfilled with Rely X ARC cement. The light activation was done using LED UltraLume 5 with 1100 mW/cm2 irradiation acting for 40 seconds. The samples were stored in environment with 100% relative humidity and 37°C for 24 hours. After this period they were submitted to the resistence test of microshear bond strength in the Instron equipament under 0,5 mm/minute of speed. The results in MPa (G1: 35.34±5.03; G2: 21.80±6.39; G3: 33.28±7.57; G4: 19.39±5.06) were submitted to analysis of variance and Tukey's test (p<0,05). The microshear bond strength resistence was significantly bigger for groups 1 and 3 (without thermocycling). There was statistically significant difference as to hydrofluoridric acid concentration. The concentration with 5% presented lower resistence to the microshear bond strength. The standard fracture analysis showed predominance of adhesive problems in all groups although groups 1 and 3 showed cohesive fractures in the cement with the biggest percentage when compared to groups 2 and 4. This way in conclusion the thermocycling decrease the resistence to microshear of the Bond union,independent of the hydrofluoridric acid concentration and the adhesive failures was predominant / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290059 |
| Date | 07 November 2011 |
| Creators | Sicoli, Eliseu Augusto, 1960- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Pezzini, Rolando Plumer, Guiraldo, Ricardo Danil, Sinhoreti, Mário Alexandre Coelho, Rontani, Regina Maria Puppin |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 59 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.3083 seconds