Previous issue date: 2011-05-23 / Novel cementing materials formulations containing flexible polymeric admixtures have been studied aiming at improving the mechanical behavior of oil well cement slurries submitted to steam injection. However, research activities in this sector are still under development. The steam injected directly into the well causes casing dilation, which after a reduction in temperature, tends to return to its original dimensions, resulting in crack formation and hydraulic isolation loss of the well, which will result in shortening of well life. In this scenario, the objective of the present study was to evaluate the mechanical behavior of Portland-based slurries containing SBR latex, applied in oil well cementing of wells submitted to steam injection. Were formulated slurries with densities of 1.797 g/cm3 (15.0 lb/Gal) and 1.869 g/cm3 (15.6 lb/Gal), containing admixtures with a latex concentration of 0; 66.88; 133.76; 200.64 and 267.52 L/m3 (0, 0.5, 1.0, 1.5 and 2.0 gpc). Tests including rheology, fluid loss control, thickening time, API compressive strength and splitting tensile strength, beyond steam injection simulation. Microstrutural characteristics of the slurries were also performed (XRD, TG, FTIR and SEM). The results showed that increasing the polymer concentration increased in the rheological properties and fluid loss, and a decrease in the elasticity modulus of the cement slurries. The results obtained showed that the slurries can be applied in cementing operations of oil wells submitted to steam injection. / Novas formula??es de pastas de cimento, aditivadas com materiais polim?ricos com caracter?sticas flex?veis, t?m sido estudadas para aplica??o em po?os sujeitos a inje??o de vapor. Entretanto, pesquisas neste setor ainda s?o atividades em desenvolvimento. O vapor injetado diretamente no po?o provoca a dilata??o do revestimento, o que ap?s redu??o na temperatura, tende a voltar as suas dimens?es iniciais, provocando forma??o de trincas e conseq?ente perda do isolamento hidr?ulico do po?o, que resultar? no encurtamento do tempo de sua vida ?til. Dentro deste contexto, este trabalho tem como objetivo estudar o comportamento mec?nico de sistemas de pastas de cimento Portland, aditivadas com l?tex SBR, para cimenta??o de po?os de petr?leo sujeitos a inje??o de vapor. Foram formuladas pastas com densidades de 1,797 g/cm3 (15,0 lb/Gal) e 1,869 g/cm3 (15,6 lb/Gal), aditivadas com concentra??o de 0; 66,88; 133,76; 200,64 e 267,52 L/m3 (0, 0,5, 1,0, 1,5 e 2,0 gpc) de l?tex. Foram realizados ensaios de reologia, controle de filtrado, tempo de espessamento, resist?ncia ? compress?o API e tra??o por compress?o diametral, al?m de simula??es de inje??o de vapor. Tamb?m foram realizadas caracteriza??es microestruturais das pastas de cimento (DRX, TG, FTIR e MEV). Os resultados mostraram que com o aumento da concentra??o do pol?mero ocorreram mudan?as nas propriedades reol?gicas e no volume de filtrado, al?m de uma diminui??o do m?dulo de elasticidade das pastas de cimento. A partir dos resultados obtidos verificou-se que as pastas podem ser aplicadas em opera??es de cimenta??o de po?os de petr?leo sujeitos a inje??o de vapor.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12720 |
Date | 23 May 2011 |
Creators | Oliveira, Filipe Silva de |
Contributors | CPF:06117988320, http://lattes.cnpq.br/3318871716111536, Martinelli, Ant?nio Eduardo, CPF:15724520800, http://lattes.cnpq.br/0022988322449627, Medeiros J?nior, Fl?vio, CPF:31698360487, Garnica, Alfredo Ismael Curbelo, CPF:05227790779, http://lattes.cnpq.br/0257037690238235, Freitas, J?lio Cezar de Oliveira, Melo, Dulce Maria de Ara?jo |
Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds