Este estudo avaliou, in vitro, tempo de endurecimento (TE), alteração dimensional (AD), solubilidade (Sl) e radiopacidade (Rp) dos cimentos AH Plus, GuttaFlow, RoekoSeal, Activ GP, Endofill e um cimento experimental à base de MTA. Para estes testes o cimentos Activ GP foi manipulado na relação pó/líquido de 28 mg para 50 µL de líquido. Para determinar o TE, moldes (10 X 2 mm) foram preenchidos com cimento e, decorridos 150 s, os cimentos foram testados com agulha tipo Gillmore (100 g), a cada 60 s, até que não houvesse marcas na superfície. Para o teste de alteração dimensional, 5 corpos-de-prova cilíndricos (3,58 x 3,0 mm) foram obtidos. Após a mensuração de seus comprimentos por meio de parquímetro digital, foram imersos em 2,24 mL de água destilada e deionizada por 30 dias e mensurados novamente. Para o teste de Sl, foram obtidos 10 corpos-de-prova (1,5 X 7,75 mm). Após serem pesados, dois a dois, foram imersos em 7,5 mL de água destilada por 7 dias e pesados novamente, determinando-se a perda percentual da massa. Os líquidos de imersão foram submetidos à espectrometria para detecção dos íons Ca2+, K+, Ni2+, Pb2+, Zn2+, Ag+. Para a Rp, 5 placas de acrílico com 4 perfurações (5 X 1 mm) foram preenchidas com cimento e, ao lado de escada de alumínio padronizada, foram radiografadas com distância foco-objeto de 30 cm e exposição de 0,2 s. A densidade radiográfica foi determinada por meio do Digora for Windows 1.51. Os resultados mostraram que os cimentos GuttaFlow e RoekoSeal estavam de acordo com a Especificação n° 57 da ANSI/ADA para os testes de TE e Rp. Em relação a ED, somente o Guttaflow estava de acordo com esta Especificação. Em relação à Sl, somente o cimento Activ GP (11,80%) não atendeu os padrões exigidos pela ANSI/ADA. A espectrometria de absorção atômica mostrou que o cimento Activ GP apresentou liberação expressiva de ions Ca2+. A liberação de ions Zn2+ foi evidenciada no cimento Activ GPl. Concluiu-se que somente cimento Guttaflow atendeu às exigências da ANSI/ADA em relação à radiopacidade, estabilidade dimensional e solubilidade. / This study evaluated, in vitro, the setting time (ST), dimensional alteration (DA), solubility (Sl) and radiopacity (Rp) of the sealers AH Plus, GuttaFlow, RoekoSeal, Activ GP, Endofill and a MTA-based experimental sealer. For these tests, the sealer Activ GP was prepared using a powder/liquid mixing ratio of 28 mg to 50 µL of liquid. In order to determine the ST, moulds (10 x 2 mm) were filled with sealer. After 150 s, the sealers were tested with a Gilmore needle (100 g) at 60-s intervals until no marks were visible on the material surface. For the DA test, 5 cylindrical specimens (3.58 x 3.0 mm) were obtained. After having their dimensions checked with a digital caliper, the specimens were stored in 2.24 mL distilled deionized water for 30 days and their dimensions were rechecked. For the Sl test, 10 specimens (1.5 x 7.75 mm) were obtained. After being weighed in pairs, the specimens were stored in 7.5 mL distilled water for 7 days and reweighed to determine the percent mass loss. The liquids in which the specimens were immersed were subjected to spectrometry for detection of ions Ca2+, K+, Na+, Ni2+, Pb2+, Zn2+and Ag+. For the Rp test, 5 acrylic plates with 4 perforations (5 x 1 mm) were filled with sealer and were radiographed near to a graduated aluminum stepwedge with 30-cm focus-object distance and 0.2-s exposure time. The radiographic density was determined using the Digora for Windows 1.51 software. The results showed that GuttaFlow and RoekoSeal were in compliance with the ANSI/ADAs specification no. 57 for the TE and Rp tests. Regarding DA, only GuttaFlow was in accordance with this specification. Regarding Sl, only Activ GP (11.80%) did not meet the ANSI/ADAs requirements. The atomic absorbance spectrometry showed that the sealer Activ GP presented significant release of Ca2+. Release of Zn2+ ions was observed for the sealer Activ GP. In conclusion, only the sealer Guttaflow met the ANSI/ADAs requirements for radiopacity, dimensional stability and solubility.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-19032010-095932 |
| Date | 17 December 2009 |
| Creators | Daniel Silva Herzog Flores |
| Contributors | Jesus Djalma Pecora, Carlos Estrela, Paulo Nelson Filho, Lea Assed Bezerra da Silva, José Roberto Vanni |
| Publisher | Universidade de São Paulo, Odontologia (Odontologia Restauradora), USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds