Orientador: Anselmo Eduardo Diniz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-13T04:02:58Z (GMT). No. of bitstreams: 1
Andrade_SergioHenrique_M.pdf: 4174934 bytes, checksum: 56bb8050f3369366b8e5e63b5735cf0b (MD5)
Previous issue date: 2009 / Resumo: O aco rapido e um material que apresenta elevada resistencia ao desgaste e elevada dureza
a quente, tendo grande aplicacao na construcao de ferramentas de dimensoes e formas complexas,
tais como brochas. O presente trabalho avaliou a utilizacao de coberturas de materiais mais
resistentes ao desgaste em brochas de aco rapido no brochamento interno de perfil, utilizando
como corpo de prova o componente do conjunto de disco de embreagem denominado cubo de
embreagem, fabricado em aco DIN C45. Foram realizados ensaios variando-se tres tipos de
revestimentos, TiN, TiCN e AlCrN, e dois tipos de substratos, o aco rapido convencional M2 e o
aco rapido sinterizado. Foram medidos o desgaste e a vida da ferramenta, a pressao no sistema
hidraulico da brochadeira e a dimensao do perfil interno do corpo de prova. A analise dos
resultados permitiu concluir que as brochas com cobertura apresentaram uma maior vida, quando
comparado com as brochas sem cobertura, mesmo quando a brocha e reafiada e nao recoberta,
trabalhando sem cobertura na superficie de saida. Entre as coberturas, o TiCN e AlCrN foram que
apresentaram melhor rendimento, apesar da pequena vantagem da cobertura de TiCN, nao foi
possivel afirmar estatisticamente que existe diferenca entre as duas coberturas. A utilizacao da
cobertura, ao contrario do esperado, causou aumento na pressao do sistema hidraulico da
brochadeira para os tres tipos de cobertura. Nao ocorreu grandes diferencas, em relacao a vida da
ferramenta, quando comparou-se as brochas com substratos de aco rapido convencional e o
sinterizado. Ficou constatado que a dimensao do perfil nao sofre grande variacao durante uma
vida da ferramenta. / Abstract: The high speed steels is a material with high wear resistance and high hot hardness, with
large application to made tools with complex shape and dimension. The present work evaluated
the application of wear resistance materials on high speed steel broach in broaching of profile,
using like specimen a clutch component denominated hub, made DIN C45 steel. It has been made
three different tests varying the coatings, TiN, TiCN and AlCrN, two different substrates, the
conventional high speed steel M2 and the powder metallurgy high speed steel. Tool wear, tool
life, pressure in the broaching machine hydraulic system and the profile dimension were
measured. The analysis of the results allowed us to conclude that the broaches with coating led to
a longer tool life than the condition without coating, the same happened when the broach was
resharpened and didn't receive a new coating, working without coating in the rake face. Between
the coatings, the TiCN and AlCrN have shown the best performances, although TiCN has a little
advantage, it wasn't possible to say statistically that there is a difference between them. The use
of coating, in the opposite was waiting, has cause the increase of the pressure in the broaching
machining hydraulic system for the three kinds of coatings. Didn't occur much difference at the
tool's life when comparing the conventional high speed steel and the powder metallurgy high
speed steel substrates. We've come to the conclusion that the profile dimension doesn't suffer
much variation during one tool's life. / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264197 |
Date | 13 August 2018 |
Creators | Andrade, Sergio Henrique |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Diniz, Anselmo Eduardo, 1959-, Ferreira, João Roberto, Novaski, Olívio |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 99 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds