Orientador: Frab Norberto Boscolo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:59:29Z (GMT). No. of bitstreams: 1
Cruz_AdrianaDiboda_D.pdf: 5672004 bytes, checksum: ac1f74246e4d3453193616e0b3d5a093 (MD5)
Previous issue date: 2009 / Resumo: No presente estudo, materiais adesivos com diferentes modos de aplicação foram submetidos à ação de radiações ionizantes de diferentes energias com o objetivo de verificar a resistência adesiva após irradiação, por meio do ensaio de microcisalhamento, avaliando o padrão de fratura, considerando se as radiações utilizadas podem ser agentes externos capazes de causar degradação da união adesiva. Após aprovação do projeto pelo comitê de ética em pesquisa (protocolo:032/2007), 60 dentes humanos tiveram as coroas seccionadas no sentido mesiodistal, e incluídas em bloco de resina epóxi. As coroas foram lixadas para exposição da dentina média obtendo 120 corpos de provas. Os corpos de prova foram divididos em 3 grupos (n=40), de acordo com os sistemas adesivos usados: SB (Adper ¿ Single Bond Plus), CB (Clearfil¿ SE Bond) e AP (Adper¿ Prompt¿ Self-Etch). Os adesivos foram aplicados em dentina e fotoativados usando LED (Lec 1000, MMoptics, 1000mW/cm2). Sobre as áreas adesivas foram colocados moldes de elastômero (0,5mm de espessura por 1,2mm de diâmetro) com três orifícios que foram preenchidos com resina composta (Filtek¿ Z-250) fotoativada por 20s. Cada grupo foi subdividido em 4 (n=10): GC= grupo controle que não foi irradiado; UV= grupo irradiado com ultravioleta; RXD= grupo irradiado com raios-X de energia para o diagnóstico; e RXT= grupo irradiado com raios-X de energia para terapia. Após irradiação foram realizados testes de microcisalhamento (Instron Inc., modelo 4411) para a avaliação da resistência adesiva, e em seguida foram avaliados os modos da fratura das amostras, classificando-os com 5 escores: 1- fratura adesiva; 2- fratura mista com 75% de exposição dentinária, 3 -fratura mista com 50% de exposição dentinária, fratura mista com 25% de exposição dentinária, e fratura coesiva. Os resultados foram submetidos à ANOVA com os testes de Tukey, Dunnett, Kruskal-Wallis e Dunn ( =0,05). As diferentes radiações ionizantes não causaram alterações na resistência da união dos adesivos CB e AP; somente o adesivo SB exibiu aumento na resistência da união após a exposição com UV (p=0,0267). A UV também alterou os padrões de fratura do adesivo SB (p=0,0000). As alterações na resistência da união adesiva e no padrão de fratura não foram degradantes, mas dependeram tanto da energia das radiações ionizantes como do modo de aplicação dos adesivos. Assim as radiações ionizantes não podem ser consideradas como agentes externos capazes de causar degradação nos materiais adesivos estudados / Abstract: In the present study, adhesive materials with different application types were exposed to ionizing radiations of varying energy with the objective to verify by means of microshear and failure mode test the bond strength after irradiation trying to determine whether the used radiations could be external agents able to degrade the adhesive bond. After approbation of this project by the Ethical Committee for Human Research (protocol number 032/2007), 60 human teeth had its crowns sectioned mesio-distally and then were included into block of epoxy resin. The crowns were sanded to show the medium dentin and to obtain 120 specimens. The specimens were divided into 3 groups (n=40), according to the adhesive systems used: SB (Adper¿ Single Bond Plus), CB (Clearfil¿ SE Bond) and AP (Adper¿ Prompt¿ Self-Etch). The adhesives were applied on dentin and photo-activated using LED (Lec 1000, MMoptics, 1000mW/cm2). Onto the bonding areas were placed customized elastomer molds (0.5 mm-thickness by 1.2mm-diameter) with three orifices which were filled with composite resin (Filtek¿ Z-250) photoactivated during 20s. Each group was subdivided into 4 subgroups (n=10): GC=control group without irradiation; UV=group irradiated with ultraviolet radiation; RXD=group irradiated with diagnostic radiation-X; RXT=group irradiated with therapeutic radiation-X. After irradiation the microshear tests were carried out (Instron Inc., model 4411) to evaluate the adhesive bond, and afterwards the modes of failure of the specimens were evaluated and classified using 5 scores: 1=adhesive failure, 2=mixed failure with 75% dentin exposed; 3=mixed failure with 50% dentin exposed; 4=mixed failure with 25% dentin exposed; 5=cohesive failure. The results were submitted to ANOVA by the Tukey, Dunnett, Kruskal-Wallis and Dunn test ( =0.05). No changes in bond strength of CB and AP were observed after application of the different radiations; only SB showed an increase in bond strength after UV (p=0.0267) irradiation. UV also changed the failure patterns in SB (p=0.0000). The changes in the adhesive bond and in the mode of failure did not show degradation, but were dependent of both the energy of ionizing radiation and the way of adhesive application. Thus, the ionizing radiation cannot be considered an external agent able to cause degradation in the studied adhesive materials / Doutorado / Radiologia Odontologica / Doutor em Radiologia Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288881 |
| Date | 12 August 2018 |
| Creators | Cruz, Adriana Dibo da |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Boscolo, Frab Norberto, 1942-, Rastelli, Alessandra Nara de Souza, Netto, Thomaz Ghilardi, Consani, Simonides, Almeida, Solange Maria de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Radiologia Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 47 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds