Atomic Layer Deposition of Copper, Copper(I) Oxide and Copper(I) Nitride on Oxide Substrates

<p>Thin films play an important role in science and technology today. By combining different materials, properties for specific applications can be optimised. In this thesis growth of copper, copper(I) oxide and copper(I) nitride on two different substrates, amorphous SiO<sub>2</sub> and single crystalline α-Al<sub>2</sub>O<sub>3</sub> by the so called Atomic Layer Deposition (ALD) techniques has been studied. This technique allows precise control of the growth process at monolayer level on solid substrates. Other characteristic features of ALD are that it produces films with excellent step coverage and good uniformity even as extremely thin films on complicated shaped substrates.</p><p>Alternative deposition schemes were developed for the materials of interest. It was demonstrated that use of intermediate water pulses affected the deposition pathways considerably. By adding water, the films are thought to grow via formation of an oxide over-layer instead of through a direct reaction between the precursors as in the case without water.</p><p>For growth of copper(I) nitride from Cu(hfac)<sub>2</sub> and ammonia no film growth occurred without adding water to the growth process. The Cu<sub>3</sub>N films could be transformed into conducting copper films by post annealing. In copper growth from CuCl and H<sub>2</sub> the water affected film growth on the alumina substrates considerably more than on the fused silica substrates. The existence of surface -OH and/or -NH<sub>x</sub> groups was often found to play an important role, according to both theoretical calculations and experimental results.</p>

Identiferoai:union.ndltd.org:UPSALLA/oai:DiVA.org:uu-4651
Date January 2004
CreatorsTörndahl, Tobias
PublisherUppsala University, Department of Materials Chemistry, Uppsala : Acta Universitatis Upsaliensis
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeDoctoral thesis, comprehensive summary, text
RelationComprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1104-232X ; 1035