Previous issue date: 2013-06-18 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / For the chemical method of synthesis of co-precipitation were produced ferrite powders manganese-cobalt equal stoichiometric formula Mn (1-x) Co (x) Fe2O4, for 0 < x < 1, first reagent element using as the hydroxide ammonium and second time using sodium hydroxide. The obtained powders were calcined at 400 ? C, 650 ? C, 900 ? C and 1150 ? C in a conventional oven type furnace with an air atmosphere for a period of 240 minutes. Other samples were calcined at a temperature of 900 ? C in a controlled atmosphere of argon, to evaluate the possible influence of the atmosphere on the final results the structure and morphology. The samples were also calcined in a microwave oven at 400 ? C and 650 ? C for a period of 45 minutes possible to evaluate the performance of this type of heat treatment furnace. It was successfully tested the ability of this group include isomorphic ferrite with the inclusion of nickel cations in order to evaluate the occurrence of disorder in the crystalline structures and their changes in magnetic characteristics.To identify the structural, morphological, chemical composition and proportions, as well as their magnetic characteristics were performed characterization tests of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDX), thermogravimetric (TG), vibrating sample magnetometry (MAV) and M?ssbauer spectroscopy. These tests revealed the occurrence of distortion in the crystal lattice, changes in magnetic response, occurrence of nanosized particles and superparamagnetism / Pelo m?todo qu?mico da s?ntese da coprecipita??o foram produzidos p?s de ferritas de mangan?s-cobalto com f?rmula estequiom?trica igual a Mn(1-x)Co(x)Fe2O4, para 0 < x <1, primeiramente utilizando como elemento reagente o hidr?xido de am?nio e, em segundo momento, utilizando hidr?xido de s?dio. Os p?s obtidos foram calcinados nas temperaturas de 400?C, 650?C, 900?C e 1150?C, em forno convencional tipo mufla com atmosfera de ar pelo per?odo de 240 minutos. Outras amostras foram calcinadas na temperatura de 900?C, em atmosfera controlada de arg?nio, para possibilitar avaliar a influ?ncia da atmosfera nos resultados finais de estrutura e morfologia. As amostras foram tamb?m calcinadas em forno de microondas nas temperaturas de 400?C e 650?C, durante per?odo de 45 minutos, possibilitando avaliar o desempenho do tratamento t?rmico neste tipo de forno. Foi testada com ?xito a capacidade de inclus?o isom?rfica deste grupo de ferrita com a inclus?o de c?tions de n?quel, permitindo avaliar ocorr?ncia de dist?rbio nas estruturas cristalinas e respectivas altera??es das caracter?sticas magn?ticas. Para identificar as caracter?sticas estruturais, morfol?gicas, de composi??o qu?mica e propor??es, bem como suas caracter?sticas magn?ticas, foram realizados ensaios de caracteriza??o de difra??o de raios X (DRX), microscopia eletr?nica de varredura (MEV), microscopia eletr?nica de transmiss?o (MET), espectroscopia de energia dispersiva (EDX), termogravimetria (TG), magnetometria de amostra vibrante (MAV) e espectroscopia M?ssbauer. Estes ensaios revelaram ocorr?ncia de distor??es na rede cristalina, altera??es de resposta magn?tica, ocorr?ncia de part?culas nanom?tricas e superparamagnetismo
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12830 |
| Date | 18 June 2013 |
| Creators | Silva, Cesar Rogerio Menezes |
| Contributors | CPF:24779953839, http://lattes.cnpq.br/9918299069511517, Paskocimas, Carlos Alberto, CPF:06296687877, http://lattes.cnpq.br/2365059843175411, Ara?jo, Jos? Humberto de, CPF:24150720444, http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4785558U2, Araujo, Jose Mario, CPF:66836484504, http://lattes.cnpq.br/3279934192221716, Moraes, M?rcio Luiz Varela Nogueira de, CPF:01157194745, http://lattes.cnpq.br/2573306822477569, Delmonte, Mauricio Roberto Bomio, CPF:27816279841, http://lattes.cnpq.br/9558299312183852, Motta, Fabiana Villela da |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds