Os materiais CaWO4:TR3+, CaMoO4:TR3+, Ca(MO4):TR3+ (TR: Pr3+, Sm3+, Eu3+, Tb3+ e Dy3+) (M: W e Mo) foram preparados pelo método da coprecipitação acoplado ao método ultrassônico a fim de estudar suas aplicações em materiais fotônicos aplicados em LEDs. Após a reação de precipitação, o material foi filtrado sob pressão reduzida, lavado com água destilada, seco e armazenado em dessecador a vácuo. Esses materiais sem tratamento térmico se mostraram como pós brancos, de aspecto uniforme, cristalinos, não higroscópicos e insolúveis em solventes polares e apolares. Após a síntese, os materiais foram submetidos a tratamento térmico em forno resistivo (1000 °C / 3 h) e sob radiação micro-ondas (5 min; ~1100 °C e 22 min; ~1200 °C). Este método oferece muitas vantagens se comparado aos métodos convencionais, tais como: método simples de operação, baixo custo, tempo curto de síntese e procedimento ambientalmente correto. Os materiais tratados sob altas temperaturas foram comparados com aqueles materiais sem tratamento térmico. Os materiais foram caracterizados pelas seguintes técnicas: espectroscopia de absorção no infravermelho (IV), análise termogravimetria (TG), difratometria de raios X - método do pó (DRX), microscopia eletrônica de varredura (MEV) e energia dispersiva de raios X (EDS). Os picos dentro do difratograma de raios X foram indexados na estrutura tetragonal scheelita I41/a. As propriedades fotoluminescentes dos compostos Ca(MO4) (M: W e Mo) dopados com Dy3+ e codopados com Eu3+ foram investigadas com base nas transições intraconfiguracionais 4f dos íons TR3+. Os espectros de excitação apresentaram bandas largas na região do UV, atribuídas às bandas de transferência de carga LMCT O→W; O→Mo e O→Eu3+. Os espectros de excitação dos fósforos dopados com Tb3+ apresentaram as bandas de absorção largas atribuídas à transferência de carga LMCT O→W6+ (5d) e O→Mo6+ (4d) sobrepostas às transições 4f8→4f75d1 do íon Tb3+ e também picos finos oriundos das transições 4f referentes aos íons Pr3+ (4f2), Sm3+ (4f5), Eu3+ (4f6), Tb3+ (4f8) e Dy3+ (4f9). O material CaWO4:Eu3+ submetido a tratamento térmico em forno resistivo (1000 °C / 3 h) apresentou o fenômeno da luminescência persistente de cor vermelha. O material triplamente dopado CaWO4:Eu3+,Tb3+,Dy3+ apresentou cores ajustáveis, indo do branco quente ao branco frio, com grande potencial para aplicação em materiais fotônicos para iluminação no estado sólido. Também, os materiais CaWO4:Eu3+,Tb3+,Dy3+ e Ca(MO4):Dy3+,Eu3+ (M: W e Mo) foram montados a base de um polímero óptico de silicone e utilizando um LED de GaN de alta potência, gerando luz branca fria e quente de altas intensidades. As coordenadas CIE (Commission Internationale l\'Eclairage) sugerem emissões multicolores dos sistemas dopados com diferentes íons TR: Pr3+, Sm3+, Eu3+, Tb3+, Dy3+. Esses materiais se mostraram promissores em aplicação de materiais de iluminação do estado sólido, com a vantagem de serem preparados de forma rápida, em poucas etapas, com alto rendimento e serem ambientalmente amigáveis. / The materials CaWO4:TR3+, CaMoO4:TR3+, Ca(MO4):TR3+ (TR: Pr3+, Sm3+, Eu3+, Tb3+ e Dy3+) (M: W and Mo) were prepared by the coprecipitation and ultrasonic method in order to study their applications in photonic materials applied in LEDs. After the precipitation reaction, the material was filtered under reduced pressure, washed with distilled water, dried and stored in vacuum desiccator. These as prepared materials were shown to be white powders, uniform in appearance, crystalline, non-hygroscopic and insoluble in polar and apolar solvents. After the synthesis the materials were submitted to thermal treatment in resistive furnace (1000 °C / 3 h) and also under microwave radiation (5 min; 1100 °C e 22 min; 1200 °C). This method offers many advantages compared to conventional methods, such as: simple operation method, low cost, brief synthesis time and environmentally correct procedure. The materials treated under high temperatures were compared with those materials without heat treatment. In the characterization of these phosphors, the following techniques were used: infrared (IR) absorption spectroscopy, thermogravimetric (TG) analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). The X-ray diffraction peaks were indexed in the scheelite tetragonal structure. The photoluminescent properties of the compounds Ca(MO4) (M: W and Mo) Dy3+ doped and Eu3+ codoped were investigated based on the intraconfiguration transitions 4f of the TR3+ ions. Excitation spectra showed broad bands in the UV region attributed to the LMCT O → W charge transfer bands; O → Mo and O Eu3+. The excitation spectra of the phosphors doped with Tb3+ showed the wide absorption bands attributed to the charge transfer LMCT O2- (2p)W6+ (5d) and O2-(2p)Mo6+ (4d) overlapping the transitions 4f8→4f75d1 of Tb3+ ion and also fine peaks originating from the 4f transitions referring to ions Pr3+ (4f2), Sm3+ (4f5), Eu3+ (4f6), Tb3+ (4f8) and Dy3+ (4f9). The CaWO4:Eu3+ material submitted to thermal treatment in a resistive oven (1000 °C / 3 h) exhibited the phenomenon of persistent red color luminescence. The triply-doped CaWO4:Eu3+,Tb3+,Dy3+ showed color matching, ranging from warm white to cool white, promising to be an excellent material to be applied in photonic materials for solid state lighting. Also, the materials CaWO4:Eu3+,Tb3+,Dy3+ and Ca(MO4):Dy3+,Eu3+ (M: W and Mo) were assembled on the basis of a silicone optical polymer and using a high power GaN LED, generating warm white and cold white light of high intensities. The CIE (Commission Internationale l\'Eclairage) coordinates suggest multicolored emissions of multicolor systems doped with various TR3+ ions: TR3+: Pr3+, Sm3+, Eu3+, Tb3+, Dy3+. These materials have proven to be promising in the application of solid state lighting materials, with the advantage of being quickly prepared, in a few steps, high performance and environmentally friendly.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-07022019-112850
Date18 October 2018
CreatorsHelliomar Pereira Barbosa
ContributorsHermi Felinto de Brito, Vera Regina Leopoldo Constantino, Marian Rosaly Davolos, Jivaldo do Rosario Matos, Paulo Cesar de Sousa Filho
PublisherUniversidade de São Paulo, Química, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0031 seconds