A two-parameter fracture criterion (TPFC) is used to correlate and predict failure loads on cracked configurations made of ductile materials. The current study was conducted to validate the use of the fracture criterion on more brittle materials, using elastic-plastic finite-element analyses with the critical crack-tip-opening angle (CTOA) failure criterion. Forman generated fracture data on middle-crack tension, M(T), specimens made of thin-sheet 7075-T6 aluminum alloy, which is a quasi-brittle material. The fracture data included a wide range of specimen widths (2w) ranging from 3 to 24 inches. A two-dimensional (2D) finite-element analysis code (ZIP2D) with a ''plane-strain core" option was used to model the fracture process. Fracture simulations were conducted on M(T), single-edge-crack tension, SE(T), and single-edge-crack bend, SE(B), specimens. The results supported the TPFC equation for net-section stresses less than the material proportional limit. However, some discrepancies were observed among the numerical results of the three specimen types. Thus, more research is needed to improve the transferability of the TPFC from the M(T) specimen to both the SE(T) and SE(B) specimens.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-5939 |
| Date | 08 December 2017 |
| Creators | Ouidadi, Hasnaa |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.0019 seconds