Influência do modo de ativação e de uma restauração simulada de porcelana no grau de conversão e na dureza superficial de um cimento resinoso auto-adesivo de cura dual / Influence of polymerization mode and a simulated ceramic restoration on degree of conversion and surface hardness of a dual-cured self-adhesive resin cement

Este estudo objetivou analisar o grau de conversão (GC) e a microdureza de um cimento resinoso utilizando diferentes protocolos de ativação, e, caracterizar o cimento quanto à composição monomérica, diâmetro médio das partículas inorgânicas e porcentagem em peso das frações orgânica e inorgânica. Foram preparados quarenta espécimes (8mm de diâmetro, 0,5mm de espessura), sendo metade usada para a determinação do GC e a outra metade usada no teste de microdureza. Os espécimes foram divididos em quatro grupos: GR1 fotoativação realizada diretamente sobre o cimento por 20s, GR2 fotoativação através de um disco de porcelana com 2mm de espessura por 20s, GR3 fotoativação através de um disco de porcelana com 2mm de espessura por 40s, e GR4 fotoativação foi omitida e o material foi polimerizado exclusivamente por seus componentes químicos. A dureza Vickers (HV) e o GC, determinado através de FTIR-ATR, foram realizados imediatamente após a fotoativação (GR1, GR2 e GR3) ou cinco minutos após o início da polimerização (GR4). Após armazenagem em ambiente seco e escuro por 24h, os espécimes foram novamente submetidos aos testes de HV e GC. Para a caracterização do material avaliado, foram realizadas as análises: Termogravimétrica, Espectrometria no Infravermelho, Espectrometria de Ressonância Magnética Nuclear e Microscopia Eletrônica de Varredura. Os resultados foram analisados estatisticamente por ANOVA, teste t e teste de Bonferroni (P≤0,05). Os valores do GC nos períodos imediato e 24h foram, respectivamente: GR1: 29.64% 4.05 / 32.58% 2.99; GR2: 27.07% 2.39 / 28.9%1 3.9 / GR3: 28.18% 3.6 / 32.34% 4.04; GR4: 7.94% 2.4 / 20.38% 4.89. Os valores de HV nos períodos imediato e 24h foram, respectivamente: GR1: 7.98HV 1.8 / 14.88HV 2.33; GR2: 4.84HV 0.13 / 9.06HV 1.63; GR3: 6.53HV 2.51 / 11.42HV 1.97. A baixa polimerização para o GR4 não permitiu a determinação da dureza inicial e após 24h este valor foi 10.65HV 0.92. O modo de ativação autopolimerizável influenciou negativamente o GC e a HV em relação ao modo de ativação no qual foi utilizada a fotoativação. A restauração simulada de porcelana não influenciou o GC, porém interferiu negativamente na microdureza. O tempo de fotoativação não influenciou os valores do GC e da HV. O GC e microdureza sofreram um aumento significativo após 24h da polimerização inicial, com exceção do GC no período inicial, quando a fotoativação foi realizada através de um disco de porcelana por um tempo de exposição de 20s. Houve uma correlação linear e positiva entre a HV e o GC para o cimento RelyX Unicem. Caracterização química: porção orgânica composta por uma mistura de monômeros, tendo o Bis-GMA como monômero-base. Presença de um monômero dimetacrilato contendo hidroxila para se ligar ao ácido fosfórico sob a forma de fosfato. Partículas inorgânicas variando entre 0,4 a 11,2m. A fração sólida do material é composta por 96% de partículas inorgânicas. Na fração líquida, a porção orgânica corresponde a 84%. Restou um resíduo incombustível de 16% devido à queima do material em atmosfera de nitrogênio. / The aim of this study was to evaluate the degree of conversion (DC) and the microhardness of a self-adhesive resin cement under different activation protocols, immediately and after 24 hours of the beginning of the polymerization, and, defining cement regarding monomer composition, average diameter of the inorganic fillers and the percentage by weight of the organic and inorganic portions. Forty specimens (8 mm in diameter, 0.5 mm in height) were prepared. Half of them were used to determine DC and the other half were used on the microhardness test. The specimens were divided into four groups: GR1 direct photoactivation for 20s, GR2 photoactivation through 2mm porcelain disc for 20s, GR3 photoactivation through 2 mm porcelain disc for 40 s, and GR4 photoactivation was omitted and curing was reliant on the chemical reaction only. Vickers microhardness (HV) and DC, by FTIR-ATR, were determined immediately after photoactivation (GR1, GR2 e GR3) or after five minutes from the beginning of the polymerization (GR4). After dry storage in the dark, for 24 hours, the samples were submitted to the tests again. In order to define the studied cement, the Thermogravimetric method was applied, as well as the Infrared Spectometry, Nuclear Magnetic Ressonance Spectroscopy and Scanning Electron Microscope. Data were statistically analyzed by one-way ANOVA, t-Test and Bonferroni Test (P≤0,05) and the degree of conversion values obtained immediately after polymerization and after 24 hours were, respectively: GR1: 29.64% 4.05 / 32.58% 2.99; GR2: 27.07% 2.39 / 28.9%1 3.9 / GR3: 28.18% 3.6 / 32.34% 4.04; GR4: 7.94% 2.4 / 20.38% 4.89. HV values obtained immediately after polymerization and after 24 hours were, respectively: GR1: 7.98HV 1.8 / 14.88HV 2.33; GR2: 4.84HV 0.13 / 9.06HV 1.63; GR3: 6.53HV 2.51 / 11.42HV 1.97. The low DC for GR4 do not permitted to quantify the initial HV value and after 24 hours this values was 10.65HV 0.92. The chemical curing mode showed DC and HV results for both period (initial and after 24 hours), statistically lower than the other groups where the photoactivation was used. The simulated ceramic restoration did not influence monomer conversion, however it negatively influence resin cement hardness. The exposure time did not influence resin cement hardness and monomer conversion. The inical DC and HV were significantly greater than after 24 hours, except for DC for initial period, when the photoactivation was realizded through a porcelain disc for 20s.There was a linear and positive correlation between degree of conversion and microhadness for the self-adhesive resin cement RelyX Unicem. Defining the cement: organic portion composed by a mixture of monomers. Bis-GMA is the main monomer. Presence of a dimethacrylate containing hydroxyl to connect to the phosphoric acid as a phosphate. Inorganic fillers raging between 0,4 to 11,2m. Powder is composed by 96% of inorganic particles. In liquid fraction, the organic portion corresponds to 84%. There were 16% of waste that did not burn due to nitrogen atmosphere.

Identiferoai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:UERJ:oai:www.bdtd.uerj.br:338
Date28 February 2008
CreatorsIrma Cunha Matos
ContributorsMauro Sayão de Miranda, Luis Claudio Mendes, Hélio Rodrigues Sampaio Filho, Rogério Luiz de Oliveira Mussel, Márcio Antônio Paraizo Borges
PublisherUniversidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Odontologia, UERJ, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0029 seconds