Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-20T10:59:33Z (GMT). No. of bitstreams: 1
Ono_Rosana_M.pdf: 4255967 bytes, checksum: beac92cd6b873a75eec9adb61e7fe7f1 (MD5)
Previous issue date: 1995 / Resumo: o propósito do presente trabalho foi avaliar "in vitro" a rugosidade superficial dos compósitos Herculite XR V (Sybron/Kerr), Z 100 (3M Co.) e Tetric (Vivadent), submetidos a diferentes procedimentos de acabamento e polimento. Foram confeccionados 24 corpos de prova de cada material, com 8mm de diâmetro por 2mm de espessura; o preenchimento da matriz foi incremental, com exposição individual
de 60 segundos, com. fotopolimerizador Visilux 2 (3M). Após o procedimento total de polimerização, os corpos de prova foram removidos da matriz e armazenados, em estUfa, a 37° C e umidade relativa de 100% por 24 horas. Após este período de tempo, cada grupo de amostras foi submetido aos procedimentos de acabamento e polimento com diferentes tipos de materiais abrasivos. Cada procedimento de acabamento e polimento foi realizado por aproximadamente 2 minutos, respectivamente com auxílio do aparelho de alta velocidade de rotação (Turbina- DABI ATLANTE), refrigerados com jatos de água/ar, com
movimentos lineares em uma única direção, e contra-ângulo (Micromotor DABI ATLANTE) em baixa velocidade de rotação, à seco. As superficies das amostras foram avaliadas antes e após cada procedimento e a leitura considerada foi a média aritmética entre os picos e vales (Ra), percorrida pelo perfilômetro (Prazis-Rug 3-Argentina), num trecho de 4,8mm. De acordo com os resultados, os procedimentos de acabamento com brocas de 30 lâminas e polimentos com Abrasivos de silicone Viking (cinza e verde) + Gel, discos Sof-Lex (fino e extrafino) e Enhance + Prisma Gloss produziram índices de rugosidade sem diferença estatisticamente significativa sobre Herculite XRV, Z 100 e Tetric. Os procedimentos de acabamento com pontas diamantadas F e FF e polimentos com Abrasivos de silicone Viking (cinza e verde) + Gel apresentaram índices de rugosidade com diferença estatisticamente significativa quando comparados aos polimentos com discos Sof-Lex (fino e extrafino) ou Enhance + Prisma Gloss, sobre I Herculite XR VeZ 100. Observou-se também que os procedimentos de acabamento com pontas diamantadas e polimentos com Abrasivos de silicone Viking (cinza e verde) + Gel, discos Sof-Lex (fino e extrafino) e Enhance não
apresentaram diferenças estatisticamente significativas sobre o compósito Tetric / Abstract: The purpose of this study was to evaluate the in vitro surface roughness of Herculite XR V, Z 100 and T etric composite samples, subjected to different finishing and polishing procedures.
A set of twenty-four 8mm diameter, 2mm thick samples was prepared for each studied material, using the incremental technique for mold filling. A sixty-second exposure to visible light was necessary to set the
samples. The activating unit used was Visilux 2 (3M). After setting, the samples were stored in an oven, at 37°C and 100% relative humidity for 24 hours. Afterwards, each group of samples was subjected to the finishing and polishing procedures with different types of materials and abrasives. E,ach finishing and polishing procedure lasted approximatel y 2 minutes. The finishing procedure was carried out with the aid of an air-water spray, high speed handpiece, moved straight on a one and on1y direction. An air-cooled, low-speed handpiece was used for the polishing procedures. The surfaces of the samples were evaluated before and after each procedure and the reading that was ~sed was the arithmetic mean value between the peaks and valleys scanned by the surface t According to t he results, the finishing procedures with 30 blade burs, and polishing with Viking (grey and green) silicone abrasives + gel, Sof Lex (fine and extra-fine) discs and Enhance + Prisma Gloss, have produced roughness indexes without significant statistical differenceS for Herculite XRV, Z 100 and Tetric. The finishing procedures with F and FF diamond points and polishing procedures with Viking (grey and green) silicone abrasives + gel showed roughness indexes with significant statistical differences when compared to the polishing procedures with Sof- Lex (fine and extra-fine) disks or Enhance + Prisma Gloss, for Herculite XRV and Z 100. It has also been observed that the finishing procedures with diamond points and polishing procedures with Viking (grey and green) silicone abrasives + gel, I Sof-Lex (fine and extra-fine) disks and Enhance + Prisma Gloss didn't show
significant statistical differences for Tetric composite / Mestrado / Materiais Dentarios / Mestre em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290090 |
Date | 23 June 1995 |
Creators | Ono, Rosana |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Almeida, Jose Vanderlei de, Goes, Mario Fernando de |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 123f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0052 seconds