Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T05:42:21Z (GMT). No. of bitstreams: 1
Guimaraes_PriscillaSantos_M.pdf: 4440699 bytes, checksum: f24c42055485725bffa0c006ac4cf4e4 (MD5)
Previous issue date: 1999 / Resumo: o propósito deste estudo foi avaliar a influência da armazenagem em água na resistência à flexão de porcelana associada a cimentos a base de resina. Para isso foram confeccionados 120 discos (21 mm de diâmetro X 2mm de espessura) de porcelana feldspática, compostos de duas camadas distintas. A primeira camada formada por porcelana de média fusão (Duceram-Degussa), seguida da aplicação da
porcelana de baixa fusão (Duceram LFC - Degussa) para completar a amostra. Todos os discos cerâmicos foram condicionados com ácido fluorídrico a 10%, durante 4 minutos e divididos em 6 grupos de 20 amostras cada. Em seguida, os materiais resinosos (Scotchbond Resin Cement - 3M, Enforce com flúor - Dentsply) foram manipulados e aplicados de acordo com as instruções dos respectivos fabricantes sobre
a superfície condicionada do disco cerâmico. Sobre o cimento recém-aplicado, foi colocada uma folha de polietileno e uma placa de vidro, e o conjunto disco cerâmico cimento-folha de polietileno e placa de vidro for posicionado em uma prensa hidráulica e comprimido com uma carga de 1500 gramas. Sob compressão o cimento foi fotopolimerizado por 20 segundos em 4 posições diametralmente opostas. Após a
remoção da carga, o cimento foi polimerizado por mais 20 segundos na região central. Os corpos-de-prova assim obtidos foram armazenados em água destilada por períodos de 24h, 3 meses e 6 meses. A seguir os corpos-de-prova foram submetidos ao ensaio de flexão biaxial, a uma velocidade de 1 mm/min, em uma máquina Instron (Modelo 4411). Os valores obtidos foram submetidos a cálculos matemáticos para deteminação da tensão de fratura. Em seguida, estes valores foram submetidos à Distribuição de Weibull, análise de variância e ao teste de Tukey. Os resultados demonstraram que não houve diferença estatisticamente significante (p<O, 01) nos valores de resistência I encontrados para os diferentes períodos de armazenagem. No entanto os grupos onde I utilizou-se o material Enforce, apresentaram valores estatisticamente superiores (p<O,01) àqueles encontrados para os grupos com o material Scotchbond. O Material Enforce I . apresentou maior módulo de Weibull e conseqüentemente, menor probabilidade de
: falha em relação ao material Scotchbond Resin Cement / Abstract: The purpose of this study was to evaluate the influence of water storage on the tensile strength of feldspathic porcelain associated to resin cements. One hundred twenty porcelain discs (21 mm in diameter x 2 mm thick) were fabricated in two different layers. The first one was done of medium fuse porcelain (Duceram - Degussa), followed by the application of a layer of low fusion porcelain (LFC -Degussa). Ali discs were conditioned with 10% fluoridric acid, for 4 minutes and divided in 6 groups of 20 samples each. After, the resin cements (Scotchbond Resin Cement - 3M, Enforce fluoride containing
Dentsply) were manipulated according to manufacturers instructions and, applied over the conditioned surface of the porcelain disco Over it a polyethylene sheet and a glass slab was placed, and the assembly was taken to a hydraulic press and squeezed with a load of 1500 g. Under compression cement was photopolimerized for 20 seconds in 4 different positions. After the removal of the load, the cement was photopolimerized for 20 seconds on the middle of the disco The samples were then stored in distilled water for 24 hours, 3 and 6 months. The biaxial flexure test was conducted in a universal test méilchine
(Instron - model 4411), at a cross speed of 1 mm/min. The data was then submitted to Tukey's test and Weibull Distribution. From the results, there was no statistic difference (p<0.01) on the strength values for the different periods of storage in water. However the strength values for groups with Enforce was statistically higher (p<0.01) than those for Scotchbond Resin Cement. The material Enforce showed a higher Weibull modulus and lower probability of failure in comparison with Scotchbond Resin Cement / Mestrado / Materiais Dentarios / Mestre em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288177 |
| Date | 18 August 1999 |
| Creators | Guimarães, Priscilla Santos |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Mandarino, Fernando, Correr Sobrinho, Lourenço |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 111p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds