Orientadores: Luis Alexandre Maffei Sartini Paulillo, Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T10:14:17Z (GMT). No. of bitstreams: 1
Souza_GraceMendoncaDiasde_M.pdf: 2850330 bytes, checksum: 6274f4312fb8638abfeedf84da268f79 (MD5)
Previous issue date: 2003 / Resumo: Quando se utilizam pinos de fibra de vidro, a porção coronária deve ser reconstruída empregando materiais estéticos como resina composta, resina modificada por poliácido, ionômero de vidro convencional ou modificado por resina, para dar proteção e estabilidade à coroa protética. Assim, o propósito deste estudo foi avaliar a resistência à fratura de raízes bovinas restauradas com pino de fibra de vidro associado a quatro materiais estéticos para núcleo, indicados para restaurações estéticas, e coroa total em resina composta indireta. Quarenta raízes bovinas tratadas endodonticamente foram inseridas em cilindros de resina poliestirênica, simulando-se o espaço do ligamento periodontal. Pinos de fibra de vidro foram cimentados com agente para cimentação resinoso e as raízes separadas em quatro grupos experimentais com dez unidades cada, de acordo com o tipo de material empregado para a confecção de núcleo: resina composta (RC), resina modificada por poliácido (RM), ionômero de vidro convencional (IV) e ionômero modificado por resina (1M). Coroas livres de metal confeccionadas em resina composta indireta - Solidex ¿ foram cimentadas sobre os núcleos sem o abraçamento radicular. As amostras foram submetidas ao carregamento tangencial de compressão após o período de sete dias de armazenamento em estufa a 37° C e 100% de umidade relativa. Os resultados obtidos foram levados à Análise de Variância (ANOVA) e ao Teste de Tukey. A ANOVA revelou haver pelo menos uma diferença estatística significativa entre as médias obtidas e o Teste de Tukey (p>0,05) mostrou que os melhores resultados de resistência à fratura foram obtidos para os núcleos em resina composta (RC - 71,97kgf - a), que não diferiram dos núcleos confeccionados em ionômero de vidro modificado por resina (IM - 62,15kgf - ab). Entretanto, este não apresentou diferença estatística do ionômero convencional (IV - 51,99kgf - b) e da resina modificada por poliácido (RM - 50,21kgf - b). A análise do padrão de fratura evidenciou que em nenhuma amostra houve fratura radicular, todas as amostras fraturaram na interface pino/núcleo / Abstract: When glass fiber posts are used, the coronary portion should be reconstructed using esthetic materials such as composite resin, polyacid-modified composite resin, conventional glass ionomer cement or resin-modified glass ionomer, in order to protect and stabilize the prosthetic crown. Therefore, the purpose of this study was to evaluate the fracture resistance of bovine roots restored with glass fiber posts associated to four core esthetic materials indicated for esthetic restorations and total crowns in indirect composite resin. Forty endodontically treated roots were inserted in polyestyrene resin cylinders, simulating periodontal ligaments space. Glass fiber posts were cemented with resin cement and the roots divided in four experimental groups with ten specimens each, according to the core material: composite resin (CR), polyacid-modified composite resin (MR), conventional glass ionomer (GI) and resin-modified glass ionomer (MI). Metal free crowns made of indirect composite resin - Solidex - were cemented onto the cores without using ferrule. The tangential load was applied to samples after a seven-day storage at 100% relative humidity and 37° C. The obtained data were subject to Analysis of Variance (ANOVA) and Tukey Test. The ANOVA results revealed that there was at least one significant statistical difference among the obtained means, while the Tukey Test (p>0.05) showed that the best results for resistance to fracture were obtained for the composite resin cores (CR - 71.97kgf - a), which did not differ from the resin-modified glass ionomer ones (MI - 62.15kgF - ab). However, there was no statistical difference among the resin-modified glass ionomer, the conventional glass ionomer (GI - 51.99kgF - b) and the polyacid-modified composite resin (MR - 50.21kgF- b). The analysis of the fracture pattems evidenced a complete absence of root fractures in the samples. On the other hand, all samples were fractured in the core/post interface / Mestrado / Dentística / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289653 |
| Date | 20 February 2003 |
| Creators | Souza, Grace Mendonça Dias de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Luís Roberto Marcondes, 1960-, Paulillo, Luis Alexandre Maffei Sartini, 1962-, Silva, Regina Celia Santos Pinto, Pereira, Gisele Damiana da Silveira |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 88f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds