Previous issue date: 2014 / Resumo: O estudo avaliou a efetividade dos antioxidantes em prevenir a degradação da interface dentina/resina ao longo do tempo. Cento e oito terceiros molares humanos foram submetidos ao modelo biológico de produção de cárie (S. mutans). Eles foram cortados perpendicularmente ao longo eixo do dente, obtendo "flats" de superfície dentinária. Os fatores avaliados são: tratamento ¿ NaOCl à 6%, EDTA, e grupo sem tratamento (Controle); sistemas adesivos - Clearfil SE Bond (SE) e Single Bond 2 (SB); e tempo de armazenamento - 24 horas (h), 12 e 18 meses. Foram construídos blocos de resina (Charisma) sobre a dentina, com altura total de 4 mm. Após 24 h imersos em água deionizada, cada espécime foi seccionado para obtenção de palitos com área média de aproximadamente 2,0 mm2 para a realização do teste de resistência de união (RU). Parte dos palitos obtidos permaneceram submersos em 1 mL de água deionizada por: 12 e 18 meses, sendo então submetidos ao teste de microtração. Os padrões de fratura foram analisados em Microscópio Eletrônico de Varredura (MEV). A nanoinfiltração, ao longo do tempo, foi avaliada por meio de fatias obtidas por secções longitudinais seriadas de outros espécimes. Estas foram imersas em solução traçadora de nitrato de prata amoniacal por 24 h, lavadas em água deionizada e imersas em solução reveladora por 8 h. Todas os espécimes foram observados em MEV para identificar os escores, de acordo com o grau de nanoinfiltração. Os resultados da RU foram analisados quanto à normalidade pelo teste Shapiro-Wilk, sendo verificada a distribuição normal dos dados e em seguida, pelo teste ANOVA Fatorial (axbxc) e teste Tukey post hoc (p<0,05). Os dados da nanoinfiltração e padrão de fratura foram analisados por estatística descritiva. Os resultados mostraram que, com relação ao tempo de armazenamento, o adesivo SB apresentou maiores valores de RU, comparado com o SE e o controle, exceto no tempo de 18 meses. Enquanto o tratamento com EDTA, apresentou maiores valores de RU nos tempo de 24 h e 12 m, e no tempo de 18 m o tratamento com NaOCl apresentou valores maiores, sendo que os dois tratamentos apresentaram valores superiores ao controle. A utilização do SB/EDTA e SE/NaOCl produziu as maiores médias de RU, sendo considerada adesivo-tratamento dependente. Os maiores percentuais do padrão de fratura foram mistos, em todos os grupos, mas, principalmente após 18 meses. Os resultados da nanoinfiltração mostraram que os sistemas adesivos utilizados, idependente do tratamento, apresentaram algum grau de nanoinfiltração porém menores que o apresentado no controle / Abstract: The study evaluated the effectiveness of antioxidants in preventing degradation of dentin/resin interface over time. One hundred and eight third human molars were submitted to a biological model of caries production (S. mutans). It was perpendicular cut to long axis of tooth to obtain a flat dentin surface. The factors evaluated were: treatment - 6% NaOCl, EDTA, and a group without treatment (Controle); adhesive systems - Clearfil SE Bond (SE) and Single Bond 2 (SB); and storage time - 24 hours (h), 12 and 18 months. Were built blocks of resin composite (Charisma) over dentin, with a total height of 4 mm. After 24 h immersed in deionized water, each specimen was sectioned to obtain sticks with an average size of approximately 2 mm2 to realize the bond strength test (µTBS). Parts of sticks obtained remain submerged in 1 ml of deionized water for: 12 and 18 months and then subjected to bond strength test. Fracture patterns were analyzed in Scanning Electron Microscopy (SEM). Nanoleakage evaluation, over time, was measured with slices obtained of serial sections of other specimens. These were embedded in tracer solution of ammoniacal silver nitrate for 24 h, washed in distilled water and immersed in a developing solution for 8 h. All samples were observed under SEM, to identify degree of nanoleakage. Results of µTBS were analyzed for normality by Shapiro-Wilk test being checked normal data distribution, and then, by Factorial ANOVA (axbxc) and Tukey post hoc test (p <0.05). Nanoleakage data and fracture pattern were analyzed using descriptive statistics. The results showed that, with respect to storage time, SB adhesive had higher RU, compared with SE and control, except in time of 18 months. Although EDTA treatment, had higher RU in time of 24 h and 12 m, and at time of 18 m NaOCl treatment showed higher values, and the two treatments were above control values. Use of SB/EDTA and SE/NaOCl produced highest RU average, being considered dependent adhesive-treatment. Largest percentage of fracture pattern was mixed, in all groups, but especially after 18 months. Nanoleakage results showed that adhesive systems used, independent counsel of treatment, showed some degree of nanoleakage but smaller than presented in control / Doutorado / Odontopediatria / Doutora em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288583 |
| Date | 24 August 2018 |
| Creators | Pacheco, Larissa Ferreira, 1983- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Correr, Gisele Maria, Rodrigues, Eliana, Paula, Andreia Bolzan de, Naufel, Fabiana Scarparo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 62 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0108 seconds