Orientador: Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T02:22:15Z (GMT). No. of bitstreams: 1
Matta_RosaVirginiaLopesda_M.pdf: 978981 bytes, checksum: 0c2e4ad14c0328dbbe5c05f7cc1e24f4 (MD5)
Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar o desempenho de um condicionador tecidual (Coe-Comfort), utilizando ou não selador de superfície, em relação às propriedades de deformação permanente e resistência à tração da união com a resina acrílica (QC-20). As amostras foram armazenadas em água destilada, numa estufa a 37±1oC. Para cada ensaio foram confeccionadas 60 amostras, separadas em 6 grupos de acordo com o tratamento e o período de armazenagem, a saber: Grupo 1- Coe-Comfort sem selador, 1 hora após armazenagem; Grupo 2- Coe-Comfort com selador, 1 hora após armazenagem; Grupo 3- Coe-Comfort sem selador, após 1 semana de armazenagem; Grupo 4- Coe-Comfort com selador, após 1 semana de armazenagem; Grupo 5- Coe-Comfort sem selador, após 2 semanas de armazenagem; Grupo 6- Coe-Comfort com selador, 2 semanas após a armazenagem. Para a confecção das amostras foram utilizadas matrizes metálicas incluídas em mufla, cujo molde impresso no silicone foi preenchido com resina acrílica e/ou condicionador tecidual. O ensaio de deformação permanente foi realizado em aparelho mecânico descrito na especificação ?18 da ADA, e o ensaio de resistência à tração, na Máquina de Ensaios Universal EMIC-DL500MF (5mm/minuto). Os dados obtidos foram submetidos à análise de variância e indicado o teste não paramétrico de Mann-Whitney, em nível de 5% de probabilidade. Para deformação permanente, foram observadas diferenças estatisticamente significantes somente após 1 semana de armazenagem, com valores mais elevados para o grupo tratado com selante de superfície. Para a resistência à tração da união, em relação ao tempo de armazenagem e ao material selador de superfície, pode-se observar que o selamento foi benéfico somente na primeira hora e na primeira semana de armazenagem. Quanto ao tipo de ruptura, após 1 hora de armazenagem, observou-se presença de ruptura do tipo adesiva em 100% das amostras, após 1 semana foi predominantemente coesiva e após 2 semanas foi coesiva em 100% das amostras. Com base nos resultados obtidos, concluímos que existiram diferenças estatisticamente significativas após uma semana de armazenagem, com valores mais elevados no grupo tratado com selante de superfície. No ensaio de resistência à tração pode-se concluir que o selamento foi benéfico ao condicionador tecidual na primeira hora e na primeira semana / Abstract: The purpose of this study was to evaluate the performance of the tissue conditioner (Coe-Comfort), with or without sealer (treatment surface), in relation to permanent deformation and tensile bond strength between resin acrylic (QC-20) and tissue conditioner. In each study there were sixty samples divided in six groups(G), according to the surface treatment and storage time in water, which were the following: G 1- Coe-Comfort without sealer, after 1 hour of stored; G 2 - Coe-Comfort with sealer, after 1 hour of stored; G 3 - Coe-Comfort without sealer, after 1week of stored; G 4 - Coe-Comfort with sealer, after 1 week of stored; G 5 - Coe- Comfort without sealer, after 2 weeks of stored; G 6 - Coe- Comfort with sealer, after 2 weeks of stored. To make the samples metallic matrixes were used invested in flasks, and models were impressed in silicone filled up with acrylic resin and/or tissue conditioner. The samples were stored in water at 37±1ºC for a determined period. The permanent deformation test was done in mechanic machine described in the ? 18 A.D.A¿s specification and the tensile bond strength test was done in a universal testing machine EMIC- DL 500 MF (5 mm/mim). The obtained data was analyzed by Mann-Whitney test at 5% of probability. To permanent deformation significant statistical differences were observed only 1 week after storage, with higher values in the group with treatment surface. To the bond strength to the traction, concerning to the time of storage samples and to the surface treatment, the sealer effect was beneficial at the conditioner only at the first hour and first week. According to the kind of failure, after 1 hour of storage, 100% of samples presented adhesive failures, after 1 week 90% of cohesive and 100% of cohesive failures after 2 weeks. We concluded that the sealer effect after 1 week of storage didn¿t have beneficial influence on permanent deformation of the tissue conditioner. To the tensile bond strength sealer effect was beneficial only in the first and second time of storage / Mestrado / Protese Dental / Mestre em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289920 |
Date | 09 January 2005 |
Creators | Matta, Rosa Virginia Lopes da |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mesquita, Marcelo Ferraz, 1967-, Junior, Manoel Gomes Troia, Consani, Rafael Leonardo Xediek |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 103f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds