Titanium dioxide nanoparticles were prepared using the sol-gel process. The effect of temperature and precursor concentration on particle size was investigated. The optimum conditions were then used to prepare carbon and nitrogen doped titanium dioxide (TiO2) nanoparticles. Doping was done to reduce band gap of the nanoparticles in order to utilize visible light in the photocatalytic degradation of organic compounds. A significant shift of the absorption edge to a longer wavelength (lower energy) from 420 nm to 456 nm and 420 nm to 428 nm was observed for the carbon doped and nitrogen doped TiO2 respectively. In this study, the prepared TiO2 photocatalyst was immobilized on carbon nanofibres to allow isolation and reuse of catalyst. The photocatalytic activity of the catalyst was tested using methyl orange as a model pollutant and was based on the decolourization of the dye as it was degraded. The doped TiO2 exhibited higher photocatalytic activity than the undoped TiO2. The materials prepared were characterized by XRD, TEM, SEM, FT-IR, DSC and TGA while the doped TiO2 was characterized by XPS, ESR and Raman Spectroscopy.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:ufh/vital:11330 |
Date | January 2011 |
Creators | Nyamukamba, Pardon |
Publisher | University of Fort Hare, Faculty of Science & Agriculture |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Type | Thesis, Masters, MSc (Chemistry) |
Format | 149 leaves; 30 cm, pdf |
Rights | University of Fort Hare |
Page generated in 0.0019 seconds