Previous issue date: 2011-07-29 / Os hidróxidos duplos lamelares (HDL) ou compostos tipo-hidrotalcita vêm sendo muito estudados devido a suas inúmeras aplicações. No campo da catálise, estes compostos podem atuar como catalisadores, suportes para catalisadores ou precursores de catalisadores. É sabido que a morfologia do suporte tem grande influência sobre a dispersão, a atividade e a seletividade apresentada pelo catalisador. Nestes caso, o conhecimento detalhado dos efeitos do suporte e dos sítios catalíticos exigem a compreensão da estrutura do HDL. Entretanto, por causa da desordem estrutural, muitas vezes inerente ao material, torna-se a determinação completa da estrutura, via difração de raios X, raramente possível. As bandas largas presentes na análise do IV, fazem a atribuição das mesmas ambígua. Devido à complexidade dos HDL e à dificuldade de se adquirir ou interpretar os resultados experimentais, foi proposto um modelo para simular as características estruturais dos compostos tipo-hidrotalcita com o politipo 3R1, usando condições periódicas de contorno e cálculos ab initio dentro da teoria do funcional da densidade (DFT). As informações estruturais da hidrotalcita, obtidas experimentalmente, foram usadas para verificar a validade do modelo teórico. Os resultados mostraram boas concordâncias com os padrões de raios X do pó experimentais. O espectro na região do infravermelho, a entalpia e energia livre de Gibbs, também foram calculadas. Os cálculos de frequências vibracionais mostraram que as moléculas de água intercaladas são altamente organizadas devido às fortes interações intermoleculares com outras moléculas de água, com ânions interlamelares e com as hidroxilas das lamelas. A presença destas interações é refletida na presença do estiramento O-H das moléculas de água deslocadas para baixas frequências. A perda da degenerescência dos modos vibracionais v3 e do v4 foi observada, indicando a redução da simetria do íon carbonato. As modificações termodinâmicas e estruturais resultantes da substituição do íon presente no HDL Zn-Al-Cl também formam analisadas. O íon Cl- do HDL precursor foi trocado por uma série de ânions como o F-, Br-, OH-, NO3-, ClO4-, CO32- e SO42-. Os resultados mostraram que a intercalação do HDL com diferentes íons, afeta o gap de energia e a basicidade da lamela tipo-brucita. A entalpia e a energia livre de Gibbs, a densidade de estados (DOS) e a densidade de estados projetada (PDOS) foram avaliadas para todos os HDL. / The layered double hydroxide (LDH) or hydrotalcite-like compounds have been widely studied due to many applications they have. In catalysis field these compounds can act as catalyst, catalyst support or precursor for supports and catalysts. It is well known that the support morphology has larger influence on the dispersion, activity and selectivity of catalysts. In this case, detailed knowledge about support effects and catalytic sites requires understanding the LDH structure. However, because of the inherent structural disorder, complete structure determination using X-ray diffraction is rarely possible. The IR analysis present broad bands, which makes their assignment ambiguous. Due to the complexity of the LDH and the difficult of acquiring experimental data, we proposed a model to simulate structural features of the hydrotalcite-like compounds with 3R1 polytypes using periodic boundary conditions and ab initio density functional theory (DFT) calculations. The structural information of hydrotalcite from experiments were used to verify the validity of theoretical model. Our results showed good agreements to the powder X-ray patterns. The infrared spectroscopy, enthalpy and Gibbs free energy, also was calculated. The IR calculations showed that intercalated water molecules are highly ordered due the strong intermolecular interactions with other water molecules, interlayer anions and layer hydroxyls. These interaction is reflected by the presence of downshift vibrational frequencies of OH-stretching of interlayer water. The loss of degeneracy of the v3 and v4 vibrational modes are observed, indicating the reduction of the carbonate anion symmetry. The thermodynamic and structural modifications derived from anion exchange on a LDH containing Zn-Al-Cl was also analyzed. The Cl- ion to the LDH precursor was exchanged for a series of anions as F-, Br-, OH-, NO3-, ClO4-, CO32- and SO42-. The resulted show that intercalation of LDH with different anions affect their gap energy and basicity of brucite-like layer. The enthalpy and Gibbs free energy, density of charge, density of state (DOS) and projected density of state (PDOS) were evaluated for all substituted materials.
Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/4461 |
Date | 29 July 2011 |
Creators | Costa, Deyse Gomes da |
Contributors | Leitão, Alexandre Amaral, Rocha, Alexandre Braga da, Capaz, Rodrigo Barbosa, Miranda, Caetano Rodrigues, Wypych, Fernando |
Publisher | Universidade Federal de Juiz de Fora (UFJF), Programa de Pós-graduação em Química, UFJF, Brasil, ICE – Instituto de Ciências Exatas |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds