Orientador: Frab Norberto Boscolo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-06T22:46:39Z (GMT). No. of bitstreams: 1
Viero_FlavioLuiz_D.pdf: 553886 bytes, checksum: 6455fb7d1e46ecd9328257967d685d33 (MD5)
Previous issue date: 2006 / Resumo: O objetivo neste estudo foi avaliar o efeito de diferentes doses de radiação X produzida a partir do Cobalto -60, em dois tipos de materiais odontológicos: o compósito Filtek TM A 110 3M, utilizado para restauração d e dentes anteriores; e o compósito condensável SureFilTM indicado para restauração cB dentes posteriores. Foram confeccionados 70 corpos de prova, dos quais 25 foram destinados ao teste de dureza Knoop e 50 ao teste de rugosidade de superfície. Depois de confeccionados, os corpos de prova foram acondicionados em caixas de acrílico e submersos em água destilada por um período de 24 horas, tendo com finalidade obter-se a estabilização química dos materiais. Após esse período, foram submetidos ao teste de Microdureza e de rugosidade de superfície. Obtidas essas medidas, os corpos de prova foram submetidos à irradiação, com as seguintes doses: 0,25Gy; 0,50Gy; 0,75Gy; 1Gy. Passadas 24 horas da irradiação, os mesmos 25 corpos de prova foram novamente submetidos ao teste de microdureza e os mesmos 50 éD teste de rugosidade. Logo após a realização do teste de rugosidade, os 50 corpos de prova foram submetidos à abrasão, sendo a seguir submersos em água destilada, permanecendo por 24 horas. Após esse período, um terceiro teste de rugosidade de superfície foi realizado nesses corpos de prova. De posse das medidas obtidas e após estas serem submetidas à análise estatística - Teste Tukey e o teste T pareado, observou-se que os tipos de compósitos irradiados apresentaram uma redução estatisticamente significante, nos valores de dureza Knoop, quando comparados ao material não irradiado; entretanto não foi observada diferença significante entre os grupos irradiados. Quando avaliada a rugosidade, observou-se que não houve diferença entre o grupo controle e o irradiado; entretanto houve diferença estatisticamente significante, dentro de cada grupo, antes e após os corpos de prova terem sido submetidos à abrasão. Conclui-se que, portanto, que a irradiação influenciou a dureza Knoop, mas não interferiu na rugosidade dos dois compósitos avaliados / Abstract: The aim of the present study was to evaluate the effects of different )f radiation doses produced by cobalt-60 teletherapy unit on two types of restorative dental materials: 3M Filtek TM A 110 used for forward teeth restorations and condensable SureFilTM used for back teeth restorations. Seventy five specimens were fabricated, 25 were submitted to Knoop hardness test and 50 to surface roughness. Next, the samples were immersed in distilled water in an acrylic support for chemical stabilization for 24 hours, and evaluated before irradiation test. Afterwards the samples were submitted to microhardness test and to surface roughness. Subsequently, samples were irradiated with single doses of 0,25Gy; O,50Gy; 0,75Gy; 1Gy. Twenty four hours after irradiation, the same samples were evaluated considering both tests - roughness and microhardness. After these procedures, the 50 samples used for the roughness surface evaluation were submitted to abrasion and stored in distilled water for 24 hours. After this period, the roughness surface were again analyzed. Data were submitted to Tukey test and to paired t-test, and it was observed that the two irradiated composites had a statistically significant reduction in Knoop hardness values when compared to nonirradiated composites adversely, no statically significant differences were found among the irradiated groups. Regarding surface roughness, no statistically significant difference was observed in the comparisons between the control group and irradiated group, however statistically significant differences were found inside each group, before and after the samples have been submitted to abrasion. It was concluded that the x-irradiation influenced the Knoop hardness, therefore it did not interfere on the surface roughness of the two restorative composite evaluated. / Doutorado / Radiologia Odontologica / Doutor em Radiologia Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288912 |
| Date | 25 July 2006 |
| Creators | Viero, Flavio Luiz |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Boscolo, Frab Norberto, 1942-, Segundo, Nilson Pena Neto, Moraes, Mari Eli Leonelli de, Moraes, Luiz Cesar de, Almeida, Solange Maria de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Radiologia Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 55f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds