Previous issue date: 2014-09-15 / Biomaterial é um termo usado para indicar os materiais que constituem as peças de
implantes médicos, dispositivos extracorporais, e descartáveis que têm sido
utilizados em medicina bem como em todos os aspectos de saúde do paciente. As
aplicações dos biomateriais são muitas e variadas, incluindo desde dispositivos de
uso prolongado, como veias e válvulas artificiais, a dispositivos de exames, como
endoscópios. Endoscopia, que significa olhar por dentro, trata-se de uma
especialidade médica que se utiliza de um equipamento chamado de endoscópio
para diagnóstico e tratamento de enfermidades. Através da endoscopia podem-se
diagnosticar enfermidades, efetuar biópsias de lesões, extrair corpos estranhos,
realizar dilatações, fazer acompanhamentos após cirurgias, passar sondas ou
cateteres, tratar sangramentos, retirar pólipos e acessar a via biliar para realizar
procedimentos cirúrgicos. Os endoscópios flexíveis possuem em sua ponta flexível
uma borracha conhecida como Fluoroelastômero Viton®. Os fluorelastômeros são
elastômeros sintéticos fluorados, conhecidos como Borracha Fluorada para serviços
em temperaturas elevadas e ambientes quimicamente agressivos. Baseado no
exposto este trabalho teve como objetivo estudar o fluorelastômero Viton® utilizado
no revestimento de ponteiras dos equipamentos endoscópicos. Foram verificadas
três grupos de amostras de ponteiras de endoscópios constituídas de Viton®
denominadas G, M e P, em sua forma virgem e tratadas com álcool etílico e HCl,
ambos concentrados, onde estas amostras foram caracterizadas por Microscopia
Óptica (MO), Microscopia Eletrônica de Varredura (MEV), Espectroscopia na Região
de Infravermelho com Transformada de Fourier (FTIR), Espectroscopia por Energia
Dispersiva de raios X (EDS), Difração de raios X (DRX), Ensaio de Ângulo de
Molhabilidade e Ensaio de Citotoxicidade. Verificou-se para todas as amostras (G, M
e P) uma superfície com morfologia granulada e irregular, com presença de
elementos contaminantes e imperfeições, com bandas características de
fluorelastômeros, difratogramas amorfos típicos de elastômeros, caráter hidrofílico e
toxicidade em meio celular exceto para a amostra M. Observou-se que o tratamento
com álcool etílico não provocou alteração estrutural no fluorelastômero agindo
apenas como eliminador de impurezas superficiais. O tratamento com HCl provocou
alterações na morfologia e estrutura química do elastômero. Verificou-se a
necessidade de adaptação da rota de produção deste fluorelastômero para
utilização como biomaterial. Foi proposta a utilização de revestimentos a base
siloxanos que possam aumentar a vida útil do fluorelastômero Viton®. / Biomaterial is a term used to indicate the materials constituting the parts of medical
implants, extracorporeal devices, disposable and which have been used in medicine
as well as in all aspects of patients' health. The applications of biomaterials are many
and varied, ranging from extended use devices such as artificial valves and veins,
the devices exams such as endoscopes. Endoscopy, which means looking inside, it
is a medical specialty that uses a device called endoscope for diagnosis and
treatment of diseases. By endoscopy can be diagnosed illnesses, perform biopsies of
lesions, extracting foreign bodies, perform dilations, do follow ups after surgery,
spend probes or catheters, to treat bleeding, remove polyps and access to the
surgical procedures biliary. Flexible endoscopes have in your flexible rubber tip one
known as Viton® fluoroelastomer. The fluoroelastomers are synthetic fluorinated
elastomers, known as Rubber Fluorinated services to high temperatures and
chemically aggressive environments. Based on the above this work was to study the
Viton® fluoroelastomer coating used on tips of endoscopic equipment. Three groups
of samples from the tips of endoscopes consist of Viton® called L, M and P, in its
virgin form and treated with HCl and ethyl alcohol, both concentrated where these
samples were characterized by Optical Microscopy (OM), Electron Microscopy Were
Verified (SEM), Spectroscopy in the Region of Fourier Transform Infrared (FTIR)
Spectroscopy Energy Dispersive X-ray (EDS), diffraction (XRD), test of Angle
Wettability and Cytotoxicity Assay rays. It was found for all samples (L, M, P) and a
surface irregular with granular morphology, presence of contaminants and
imperfections, characteristic bands of fluoroelastomers, typical XRD of amorphous
elastomers, hydrophilic, and toxicity in cell except for M. In the sample was observed
that treatment with ethanol did not cause structural changes in the fluoroelastomer as
scavenger only surface impurities. Treatment with HCl caused changes in the
morphology and chemical structure of the elastomer. There was a need to adapt the
production of fluoroelastomer route for use as a biomaterial. The use of coatings
siloxanes base that can increase the life of Viton® fluoroelastomer was proposed.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/355 |
| Date | 10 April 2018 |
| Creators | LIMA, Vanessa Sena Correia. |
| Contributors | FOOK, Marcus Vinícius Lia., HOLANDA, Adriana Lima de., BARBOSA, Rossembergo Cardoso. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds