Orientador: Maria Isabel Felisberti / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-26T18:00:04Z (GMT). No. of bitstreams: 1
Trinca_RafaelBergamo_D.pdf: 7109183 bytes, checksum: 36f8cbad69a4e17b2adb60ccbc082e94 (MD5)
Previous issue date: 2015 / Resumo: Este trabalho teve como objetivo a síntese e a caracterização de poliuretanas segmentadas (SPUs), baseadas em macrodióis de baixa massa molar (2 kDa) ¿ poli(etileno glicol), poli(L-lactídeo) e poli(carbonato de trimetileno) (PEG, PLLA e PTMC, respecti- vamente) ¿ e diferentes diisocianatos (2,4-diisocianato-tolueno e 1,6-diisocianato-hexano, 2,4-TDI e HDI, respectivamente) e extensores de cadeia (1,4-butanodiol e ácido-2,2-bis(hidroximetil)-propanóico BDO e DMPA, respectivamente). Os macrodióis PLLA e PTMC foram sintetizados por polimerização por abertura de anel (ROP). As SPUs foram obtidas por uma rota de duas etapas: pré-polimerização dos macrodióis com diisocianatos e extensão de cadeia. Estudou-se os efeitos da razão mássica entre os macrodióis sobre as propriedades físico-químicas e morfológicas de SPUs mono, bi e tricomponentes baseadas em 2,4-TDI e BDO. Análises de ¹H NMR e GPC revelaram diferenças na reatividade dos macrodióis, que resultaram em diferenças de composição das SPUs em relação ao meio reacional e na distribuição de massa molar. Análises por DSC, DMTA, AFM e ensaios de intumescimento revelaram que as propriedades intrínsecas dos precursores foram combinadas e moduladas nas SPUs. A combinação dos três macrodióis resultou em SPUs com propriedades únicas, não encontradas nas SPUs binárias e monocomponentes. Os efeitos da natureza de diisocianatos e extensores de cadeia sobre as propriedades de SPUs ternárias também foram estudados. As SPUs baseadas em diisocianatos simétricos (HDI) apresentam temperatura de transição vítrea inferior aos baseados em 2,4-TDI, além disso, essas SPUs são semicristalinas, enquanto as baseadas em 2,4-TDI são essencialmente amorfas. A morfologia das SPUs, tipicamente de fase dispersa em uma matriz, é afetada pela proporção entre os macrodióis e pela natureza dos diisocianatos e dos extensores de cadeia. A capacidade das SPUs em intumescer em água é governada pelo teor de PEG e varia com a temperatura (SPUs termo-responsivas) enquanto as SPUs baseadas em DMPA apresentaram intumescimento dependente do pH do meio (SPUs responsivas ao pH). SPUs com menor teor de PEG e ricas em PLLA foram processadas pela técnica de eletrofiação, resultando em filmes nano fibrosos e porosos com propriedades elastoméricas / Abstract: This study aimed at the synthesis and characterization of segmented polyurethanes (SPUs), based on low molecular weight (2 kDa) macrodiols ¿ poly(ethylene glycol), poly(L-lactide) and poly(trimethylene carbonate) (PEG, PLLA and PTMC, respectively) - and different diisocyanates (2,4-diisocyanato-toluene and 1,6-diisocyanato-hexane, 2,4-TDI and HDI, respectively) and chain extenders (1,4-butanediol and 2,2-bis-hydroxymethyl-propanoic acid, DMPA and BDO respectively). The PLLA and PTMC macrodiols were synthesized by ring-opening polymerization (ROP). The SPUs were obtained by a two-step route: synthesis of prepolymers from diisocyanates and macrodiols, followed by a chain extension step. The effects of the weight ratio of macrodiols on the physico-chemical and morphological properties of SPUs based on 2,4-TDI and BDO were studied. The ¹H NMR and GPC analysis revealed differences in reactivity of macrodióis, which resulted in differences in composition of the SPUs in relation to the reaction medium and in the molar mass distribution. Analysis by DSC, DMTA, AFM and swelling assays revealed that the intrinsic properties of the precursors were combined and modulated in SPUs. The combination of the three macrodiols results in SPUs with unique properties not found in binary and single component SPUs. The effects of the nature of the chain extenders and diisocyanates on the properties of ternary SPUs were also studied. The SPUs based on symmetrical diisocyanates (HDI) presents lower glass transition temperatures than those based on 2,4-TDI. Moreover, they are semi crystalline while SPUs based on 2,4-TDI are essentially amorphous. The morphology of the SPUs, typically of a dispersed phase in a matrix, is affected by the macrodiols ratio and by the nature of diisocyanates and chain extenders. The water swelling capability of the SPUs is governed by the PEG content and varies with temperature (temperature responsive SPUs) as well as with pH (pH responsive SPUs) when BDO is replaced with DMPA. SPUs with low PEG content and rich in PLLA were processed by electrospinning technique, resulting in nanofibrous porous films with elastomeric properties / Doutorado / Físico-Química / Doutor em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248782 |
Date | 26 August 2018 |
Creators | Trinca, Rafael Bergamo, 1987- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Felisberti, Maria Isabel, 1959-, Hui, Wang Shu, Abraham, Gustavo Abel, Sabadini, Edvaldo, Pessine, Francisco Benedito Teixeira |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
Source Sets | IBICT Brazilian ETDs |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 93 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.028 seconds