Orientador: João Manuel Domingos de Almeida Rollo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-13T23:36:24Z (GMT). No. of bitstreams: 1
CorrerSobrinho_Lourenco_M.pdf: 4734512 bytes, checksum: 569f73a3e6dcab008c7d35d1b1176426 (MD5)
Previous issue date: 1991 / Resumo: No presente estudo foi elaborada uma liga EXPERIMENTAL à base de Cu-Al-Zn-Nb, onde os elementos de maior ponto de fusão que compõem a liga EXPERIMENTAL, foram adicionados na forma de pó. Alguns ensaios foram realizados, como: análise química. Dureza Vickers, análise metalográfica, corrosão através da análise eletroquímica potenciocinética, contração de fundição, fluidez e tração. A análise química foi realizada por via úmida, enquanto o ensaio de Dureza Vickers numa máquina Vickers Limited, e a metalografia num aparelho NEOPHOT 21 (CARL ZEISS). Já os testes de corrosão foram realizados num aparelho tipo CORROSCRIPT - TUCUSSEL e a contração de fundição em um anel metálico similar ao utilizado por 'EARNSHAW POT.10'. Para o ensaio de fluidez, foram utilizadas telas de nylon similares, a usada por 'PRESSWOOD POT.36'. O ensaio de tração foi efetuado numa máquina de ensaio UNIVERSAL LOSENHAUSENWERK de acordo com a especificação n. 5 da 'A.D.A. POT.1'. Este estudo foi desenvolvido, comparando-se os resultados da liga EXPERIMENTAL com os obtidos de duas ligas comerciais à base de cobre DURACAST MS e GOLDENT LA. Para obtenção dos corpos de prova foi utilizada a técnica de fundição odontológica pelo método da cera perdida. As fundições foram executadas através de um maçarico gás-oxigênio numa centrifuga convencional. Os resultados da análise metalográfica revelaram que não houve a formação de solução sólida nas três ligas estudadas. A liga EXPERIMENTAL e DURACAST MS apresentaram uma resistência à corrosão superior à liga GOLDENT LA. Quanto à Dureza Vickers, a liga EXPERIMENTAL apresentou um valor maior em relação às outras duas ligas. O valor da contração de fundição da liga DURACAST MS foi superior e a liga EXPERIMENTAL apresentou valores de fluidez superiores em relação às duas ligas comerciais. Já para o ensaio de tração, a liga EXPERIMENTAL foi superior e a liga GOLDENT LA apresentou maior valor de alongamento em relação às outras duas ligas / Abstract: In the present study it was been developed an experimental alloy fo the Cu-Zn-Al-Nb base. Where the elements the most point of fusion, that compose the experimental alloy where odds in a power form. Some experiments were made, such as: metallographic analysis, corrosion by test eletrochemical potenciocinetic analysis, castability test, tensile test, casting of shrinkage, chemical analysis and Hardness Vickres. The chemical analysis has been made through moist medium, while the Hardness Vickers experiment has been made in a machine Vickers Limited and the metallographic analysis in a device called NEOPHOT 21 (CARL ZEISS). And the corrosion test has been realized in a device called Corroscript Tucussel and the casting of Shrinkage in a metal ring similar to the one used by 'EARNSHAW IND POT.10¿. For the castability test it was used nets of nylon similar to the one used by 'PRESSWOOD POT.36' and the tensile experiment was realized in a machine of the Universal test LOSENHAUSENNERK according to the expecification n. 5 of 'A. D. A. POT.1'. All this study was developed comparing the results of the experimental alloy with ones obtained with two comercial alloys to the base of copper DURACAST MS and GOLDENT LA. In order to obtain test samples, the routine dental casting tecnique, was used with lost wax method. The castings were executed through a gas/oxigen blowpipe in conventional centrifuge. The results from the metalographic analysis has revealed that there hasn't been formation of a solid solution in the three studied alloys. Lhe EXPERIMENTAL and de DURACAST MS alloys have presented a resistance to corrosion superior to the GOLDENT LA alloy. Concerning the Hardness Vickers, the EXPERIMENTAL alloy has presented a bigger value in relation to the other two alloys. The value of casting Shrinkage of the DURACAST MS alloy was superior and the EXPERIMENTAL alloy has presented superior values of castability in relation to the comercial alloys. And for the tensile test the EXPERIMENTAL alloy was superior and the GOLDENT LA alloy has presented a bigger alongation value in relation to the other two alloys / Mestrado / Materiais Dentarios / Mestre em Odontologia
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289327 |
Date | 13 July 2018 |
Creators | Correr Sobrinho, Lourenço, 1960- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Rollo, João Manuel Domingos de Almeida |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | [134]f : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds