Estudo qualitativo dos aspectos morfológicos e químicos dos produtos da oxidação a altas temperaturas de um aço Cr-10/Ni-11 após tratamentos superficiais com laser e jateamento com microesferas de vidro.

Description

Submitted by Maurílio Figueiredo ([e-mail]) on 2014-09-12T19:07:03Z
No. of bitstreams: 2
license_rdf: 22190 bytes, checksum: 19e8a2b57ef43c09f4d7071d2153c97d (MD5)
DISSERTAÇÂO_EstudoQualitativoAspecto.pdf: 12316190 bytes, checksum: 03223c5b98deecacffd108761eef6cb7 (MD5) / Approved for entry into archive by Gracilene Carvalho ([e-mail]) on 2014-11-05T15:35:31Z (GMT) No. of bitstreams: 2
license_rdf: 22190 bytes, checksum: 19e8a2b57ef43c09f4d7071d2153c97d (MD5)
DISSERTAÇÂO_EstudoQualitativoAspecto.pdf: 12316190 bytes, checksum: 03223c5b98deecacffd108761eef6cb7 (MD5) / Made available in DSpace on 2014-11-05T15:35:31Z (GMT). No. of bitstreams: 2
license_rdf: 22190 bytes, checksum: 19e8a2b57ef43c09f4d7071d2153c97d (MD5)
DISSERTAÇÂO_EstudoQualitativoAspecto.pdf: 12316190 bytes, checksum: 03223c5b98deecacffd108761eef6cb7 (MD5)
Previous issue date: 2013 / No presente trabalho foi realizado o estudo da influência dos tratamentos superficiais Shot peening (SP), Laser peening (LP) e Refusão a Laser (RL) na oxidação de tubos de aço Cr- 10/Ni-11 utilizados como trocadores de calor. Na realização do tratamento SP foram utilizadas microesferas de vidro para jateamento da amostra, durante um intervalo de tempo de 90s. Para as amostras tratadas por LP e RL foi utilizado um laser pulsado de Nd:YAG. Para o primeiro caso, o laser operou a 1400V, com pulsos de energia da ordem de 350mJ e frequência igual a 1,0Hz. Observou-se, por meio de microscopia óptica, a deformação plástica sobre a superfície da amostra após o tratamento LP. No segundo caso, quatro amostras foram irradiadas por um feixe laser em modo contínuo, a uma potência de 24W e a uma frequência de pulsação de 5,0kHz. Em seguida, as amostras submetidas aos três tratamentos foram oxidadas a 750°C (1023K) em atmosfera de ar saturado com vapor d’água, por 30h. Os dados obtidos por MEV/EDS revelaram a formação de óxidos a base de cromo na amostra tratada por SP e, principalmente, de ferro para as amostras submetidas aos três tratamentos superficiais. De uma maneira geral, sobre as áreas afetadas pelos tratamentos, foi possível observar a formação de um maior volume de óxidos com morfologias bem heterogêneas, comparativamente àqueles formados sobre as regiões não tratadas. __________________________________________________________________________________________ / ABSTRACT: In the present work was to study the influence of surface treatments Shot peening (SP), aser
peening (LP) and Laser remelting (LR) in the oxidation of Cr-10/Ni-11 steel tubes used as eat exchangers. In effecting treatment SP glass beads were used to blast the sample during a
time interval of 90s. For the samples treated with LP and RL was used a pulsed laser Nd: YAG. For the first case, the laser operated at 1400V with energy pulses of about 350mJ and
frequency equal to 1,0Hz. The plastic deformation on the surface of the sample was observed by optical microscopy after treatment LP. In the second case, four samples were irradiated by a laser beam in continuous mode, at a power of 24,0W and a frequency pulse of 5,0kHz. Then the samples subjected to three treatments were oxidized at 750°C (1023K) in an air atmosphere saturated with water vapor for 30h. The data obtained by SEM / EDS analysis revealed the formation of chromium oxides in the SP base treated sample and primarily iron oxides in the samples subjected to three surface treatments. Generally, on the areas affected by the treatments it was possible to observe the formation of a greater volume of oxides with heterogeneous morphology compared to those formed on the untreated regions

Links & Downloads

1. CASTRO< H. X. de. Estudo qualitativo dos aspectos morfológicos e químicos dos produtos da oxidação a altas temperaturas de um aço Cr-10/Ni-11 após tratamentos superficiais com laser e jateamento com microesferas de vidro.. 2013. 82f. Dissertação (Mestrado em Engenharia de Materiais) – Universidade Federal de Ouro Preto, Ouro Preto, 2013.
2. http://www.repositorio.ufop.br/handle/123456789/3684

Tags

Lasers

Tubos

Oxidação

Engenharia de materiais.

Additional Fields

Identifer	oai:union.ndltd.org:IBICT/oai:localhost:123456789/3684
Date	January 2013
Creators	Castro, Hugo Xavier de
Contributors	Costa, Adilson Rodrigues da
Source Sets	IBICT Brazilian ETDs
Language	Portuguese
Detected Language	Portuguese
Type	info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Source	reponame:Repositório Institucional da UFOP, instname:Universidade Federal de Ouro Preto, instacron:UFOP
Rights	Autorização concedida ao Repositório Institucional da UFOP pelo autor(a), 08/09/2014, com as seguintes condições: disponível sob Licença Creative Commons 3.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta., info:eu-repo/semantics/openAccess