Previous issue date: 2015-12-19 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / O presente estudo, dividido em três artigos, teve como objetivo investigar propriedades ópticas e mecânicas de materiais cerâmicos utilizados no sistema CAD-on. No primeiro artigo, foram confeccionadas barras monolíticas e tricamadas obtidas pela técnica CAD-on e submetidas ao teste de flexão por três pontos para avaliar resistência flexural, módulo de Weibull, modo de falha (mensurando o tamanho do defeito crítico em microscopia eletrônica de varredura – MEV) e tenacidade de fratura. No segundo artigo, foram confeccionadas próteses parciais fixas (PPFs), pela técnica CAD-on as quais foram submetidas ao teste e carga máxima de fratura "fast fracture" e ensaio de vida acelerado "step stress", sendo avaliados a confiabilidade e o modo de falha das PPFs por MEV. Já no terceiro artigo, discos cerâmicos para o sistema CAD-on foram utilizados para avaliar o efeito da combinação de cerâmicas de infraestrutura (zircônia) e de cobertura (dissilicato de lítio) na capacidade de mascaramento de substratos dentais e fundos metálicos. No primeiro artigo, as barras monolíticas e tricamadas tiveram resultados estatisticamente semelhantes para resistência flexural, resistência característica e módulo de Weibull, no entanto, os valores de tenacidade e o defeito crítico e das barras tricamadas foram significativamente superiores comparados às barras monolíticas. No segundo artigo, as PPFs tiveram dois modos de falha, lascamento e fratura do conector. O valor do módulo de Weibull (?) foi de 7,8 quando combinado os dois modos de falha. Quando analisados separadamente lascamento e fratura do conector, os valores de ? foram de 7,9 e 2,9, respectivamente. No teste "step stress", os valores de ? foram de 1,6 quando houve falha do conector e 1,3 quando houve lascamento. No terceiro artigo, a redução da espessura dos espécimes de dissilicato de lítio determinou aumento significativo da translucidez e, quanto menor a espessura, menor a capacidade de mascaramento dos conjuntos cerâmicos, independente do substrato utilizado. As principais conclusões deste estudo foram: 1) barras monolíticas e tricamadas não mostraram diferença estatística nos parâmetros avaliados, com exceção do tamanho de defeito crítico e tenacidade; 2) o teste de fadiga influenciou significantemente a confiabilidade das PPFs confeccionadas utilizando o sistema CAD-on; 3) a redução de espessura da camada de dissilicato de lítio, a presença de infraestrutura de zircônia e os substratos metálicos tiveram maior influência nas propriedades ópticas das restauração cerâmicas. / The aim of this study, divided into three papers, was to investigate the optical and mechanical properties of ceramic materials used in the CAD-on system. In the first paper, monolithic and trilayer bars were obtained by the CAD-on technique and subject to three-point bending test to evaluate flexural strength, Weibull modulus, failure mode (measuring the critical defect size by scanning electron microscopy – SEM) and fracture toughness. In the second paper, fixed partial dentures (FPDs) were prepared by the CAD-on technique and subjected to fast fracture (monotonic loading) or step stress (simulating cyclic fatigue) tests, evaluating the reliability and failure mode of the FPDs by SEM. In the third paper, ceramic discs for the CAD-on system were used to evaluate the combination of framework ceramic (zirconia) and veneer ceramic (lithium dissilicate) on the masking abilty of dental and metallic backgrounds. In the first paper, the monolithic and trilayer bars had statistically similar results for flexural and characteristic strength, and Weibull modulus; however the toughness and critical defect size of trilayer bars were significantly higher compared to monolithic bars. In the second paper, the FPDs had two failure modes, chipping and connector fracture. The Weibull modulus (?) was 7.8 when combined the two failure modes. When analyzing chipping and connector fracture separately, the ? values were 7.9 and 2.9, respectively. In the step stress test, ? values were 1.6 for connector failure and 1.3 for chipping. In the third paper, reduction in lithium dissilicate thickness determined a significant increase in translucency. Lower thickness also reduced the masking ability of the ceramic combinations, regardless of the substrate used. The main conclusions of this study were: 1) monolithic and trilayer bars showed no statistical differences in the parameters evaluated, with the exception of critical defect size and toughness; 2) the fatigue test significantly influenced the reliability of the FPDs obtained by the CAD-on technique; 3) reduction in the lithium dissilicate thickness and the presence of zirconia framework and metal substrates had greater influence on the optical properties of the ceramic restorations.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3517 |
| Date | 19 December 2015 |
| Creators | Basso, Gabriela Romanini |
| Contributors | 42784263053, http://lattes.cnpq.br/7064579792237750, Moraes , Rafael Ratto de, Della Bona, Álvaro |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds