Submitted by Márcio Ropke (ropke13marcio@gmail.com) on 2017-06-21T13:55:48Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Influência da formulação e translucidez na estabilidade de cor e eficiência de.pdf: 1165017 bytes, checksum: 779397a9ef1b2fbad08ba861a1f39ee1 (MD5) / Made available in DSpace on 2017-06-21T13:55:48Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Influência da formulação e translucidez na estabilidade de cor e eficiência de.pdf: 1165017 bytes, checksum: 779397a9ef1b2fbad08ba861a1f39ee1 (MD5)
Previous issue date: 2016-06-23 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / O objetivo deste estudo, dividido em duas etapas, foi investigar a influência da composição e da translucidez de compósitos odontológicos na estabilidade de cor e eficiência de polimerização. A primeira etapa envolveu a formulação de compósitos experimentais com a proposição de determinar a relação entre o sistema fotoiniciador e o conteúdo inorgânico sobre a estabilidade de cor e a eficiência de polimerização. Três sistemas fotoiniciadores foram empregados (canforquinona/amina – CQ/amina; óxido mono-alquil fosfínico - TPO e óxido bis-alquil fosfínico - BAPO) e dois tamanhos médios de partículas de sílica como carga (7nm ou 16nm). A eficiência de polimerização foi analisada pela dureza Knoop a 25kgf/mm2 por 15s utilizando microdurômetro. A estabilidade de cor foi calculada pela fórmula de diferença de cor CIELAB, mensurada com espectrofotômetro. Os materiais foram submetidos ao envelhecimento pela imersão em água e em solução de café. Os dados foram submetidos à Análise de Variância, seguidos pelo teste de Student-Newman-Keuls (a=0,05). Os materiais formulados com TPO apresentaram maior estabilidade de cor. O tamanho da partícula não influenciou os resultados da estabilidade de cor. A eficiência de polimerização não foi influenciada pelo sistema fotoiniciador ou pelo tamanho da partícula de carga. A segunda etapa deste projeto envolveu a avaliação de quatro compósitos comerciais (IPS Empress Direct, Estelite S Quick, Filtek Z350 XT e Opallis), com diferentes níveis de translucidez, com a proposição de verificar a relação entre o nível de translucidez e a estabilidade de cor, assim como entre o nível de translucidez e a eficiência de polimerização. A eficiência de polimerização foi analisada pelo grau de conversão de C=C utilizando espectroscopia no infravermelho transformada de Fourier, enquanto a estabilidade de cor foi avaliada pela fórmula de diferença de cor CIEDE2000. Os dados foram submetidos à Análise de Variância e teste de Student-Newman-Keuls (a=0,05). Foi observado que quanto maior a translucidez, menor a estabilidade de cor dos compósitos odontológicos, apesar de não ter sido observada diferença significativa em relação à eficiência de polimerização. De acordo com os resultados dos estudos pode ser concluído que o sistema fotoiniciador, o tamanho das partículas de carga e a translucidez afetaram a estabilidade de cor dos compósitos odontológicos apesar de não ter sido observada influência destes sobre a eficiência de polimerização. / The objective of this study, separated in two phases, was to investigate the process related to resin-based composites’ formulation and translucency over the color stability and cure efficiency. The first phase involved experimental resin-based composite formulations with the purpose to determine the relationship between the photoinitiator system and inorganic content over the color stability and cure efficiency. Three different photoinitiator systems were used (camphorquinone/amine – CQ/amine, monoalquil oxide – TPO, and bisalquil oxide – BAPO) and two average silica nanofiller sizes (7 nm or 16 nm). The cure efficiency was analyzed by Knoop hardness reading under 25kgf/mm² for 15s using a microindenter. The color stability was measured by CIELAB color difference formula measured with a spectrophotometer. The materials were aged by immersion in water and coffee solution. Data were submitted to Analysis of Variance followed by Student-Newman-Keuls’ test (a=0.05). TPO-based materials presented the higher color stability. The filler size did not influence the color stability results. The cure efficiency was not influenced by photoinitiator system or filler size. The second phase involved four commercial resin-based composites (IPS Empress Direct, Estelite S Quick, Filtek Z350 XT and Opallis) tested in different translucent degrees with the purpose to determine the relationship between translucency and color stability and between translucency and cure efficiency. The cure efficiency was analyzed by degree of C=C conversion using Fourier-transformed infrared spectroscopy. The color stability was measured by CIEDE2000 color difference formula. Data were submitted to Analysis of Variance and Student-Newman-Keuls’ test (a=0.05). It was observed that the higher the translucency, the lower the color stability, despite no significant difference in cure efficiency results. Based on the results from both studies, it can be concluded that the photoinitiator system, filler-particle size and translucency affect the color stability of resin-based composites although no significant influence on the cure efficiency was observed.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3569 |
| Date | 23 June 2016 |
| Creators | Salgado, Vinícius Esteves |
| Contributors | 95962395034, http://lattes.cnpq.br/0746540134841865, Moraes, Rafael Ratto de, Schneider, Luis Felipe Jochims |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds