Orientador: Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T03:54:21Z (GMT). No. of bitstreams: 1
Resende_CristinadoAmparo_M.pdf: 828266 bytes, checksum: 67ff65721ab9a2c7931bd0a2be4a3001 (MD5)
Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar a influência da altura do remanescente coronário e de diferentes tipos de retenções intra-radiculares na resistência à fratura de raízes bovinas restauradas com coroas totais confeccionadas em resina composta laboratorial nas seguintes condições: ausência de remanescente coronário ou presença de um ou dois milímetros e cinco métodos de retenção intra-radicular. Cento e cinqüenta dentes bovinos foram selecionados padronizando-se as dimensões das raízes. As coroas foram seccionadas e as raízes remanescentes receberam tratamento endodôntico e foram divididas, aleatoriamente, em quinze experimentais (n=10): G1 - pino de fibra de vidro (FV) e 0 mm; G2 - FV e 1 mm;
G3 - FV e 2 mm; G4 - pino pré-fabricado metálico (PM) e 0 mm; G5 - PM e 1 mm; G6 - PM e 2 mm; G7 - pino de fibra de carbono (FC) e 0 mm; G8 - FC e 1 mm; G9 - FC e 2 mm; G10 - núcleo metálico fundido (NMF) e 0 mm; G11 - NMF e 1 mm; G12 - NMF e 2 mm; G13 ¿ preenchimento do canal radicular com resina composta (RC) e 0 mm; G14 - RC e 1 mm; G15 - RC e 2 mm. As coroas totais foram cimentadas com cimento resinoso e as raízes foram fixadas em resina poliestirênica, simulando-se o ligamento periodontal com material de moldagem à base de poliéter. As amostras
foram submetidas ao carregamento tangencial de compressão, sob um ângulo de 135o a 0,5 mm/min até ocorrer a fratura. Os resultados (ANOVA / Tukey a=0,05) demonstraram que na ausência de remanescente, o grupo RC apresentou os maiores valores de resistência à fratura, não diferindo estatisticamente dos grupos restaurados com FC, FV e PM; o grupo restaurado com NMF apresentou os menores valores médios de resistência à fratura. Na presença de 1 mm de remanescente o grupo PM apresentou os maiores valores de resistência à fratura, não diferindo estatisticamente dos grupos restaurados com FV, NMF e RC e o grupo FC apresentou os menores valores médios. Na presença de 2 mm de remanescente, os diferentes tipos de retenções não promoveram diferenças entre os valores médios de resistência à fratura. Para os grupos restaurados com FV, FC e NMF, a altura do remanescente não influenciou nos resultados. Para os grupos PM, a altura de 1 mm proporcionou os maiores valores de resistência à fratura e o grupo com 2 mm de remanescente apresentou os menores valores. No grupo RC, a ausência de remanescente dental coronário promoveu os melhores resultados e o grupo com 1 mm de remanescente apresentou os piores resultados. A análise geral dos padrões de fratura demonstrou que 68% das fraturas atingiram os terços apical ou médio. Os grupos restaurados com pinos de fibra de vidro apresentaram os melhores padrões de fratura, enquanto os restaurados apenas com resina composta apresentaram os piores padrões de fratura / Abstract: The purpose of this study was to evaluate the influence of dental coronal structure height and different types of intraradicular retention on the fracture strength of bovine roots restored with total crowns made of laboratory composite resin under the following conditions: absence of dental coronal structure or presence of one or two millimeters, and five methods of intraradicular retention. One hundred fifty bovine teeth were chosen and the canal size was standardized. The crowns were sectioned and the canals were treated endodontically and the specimens distributed randomly into 15
experimental groups: G1 ¿ fiberglass post (FV) and 0 mm; G2 ¿ FV and 1 mm; G3 ¿ FV and 2 mm; G4 ¿ prefabricated metal post (PM) and 0 mm; G5 ¿ (PM) and 1 mm; G6 ¿ (PM) and 2 mm; G7 ¿ carbon fiber post (FC) and 0 mm; G8 ¿ (FC) and 1 mm; G9 ¿ (FC) 1 mm; G15 ¿ RC and 2 mm. Total crowns were luted with resin cement and the roots were fixed in resin blocks and artificial periodontal ligament was simulated with casting
material made of polyether. The specimens were submitted to compressive strength test at 135o and 0.5 mm/min until fracture occurred. The results (ANOVA / Tukey a=0.05), showed that in absence of dental coronal structure, the group RC presented the most fracture strength values, not differing statistically from groups restored by FC, FV and PM, and the group restored by NMF presented the lowest mean values. In the presence of 1 mm, Group PM presented the highest fracture strength values, not differing statistically from groups restored by FV, NMF and RC, and the group restored by FC presented the lowest mean values. In the presence of 2 mm, the different types of intraradicular retentions did not cause differences among mean fracture strength values. In the groups restored by FV, FC and NMF, the dental coronal structure height had no influence on the results. In the PM group, the height of 1 mm, showed the highest and the group with 2 mm presented the lowest mean values. In the group RC the absence of dental coronal structure showed the best results and the group with 1 mm presented the worst results. The general fracture pattern analysis showed that 68% of fractures involved the gingival and apical thirds. The groups restored by FV showed the best fracture patterns, and the groups restored by RC, the worst / Mestrado / Dentística / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289722 |
| Date | 24 January 2005 |
| Creators | Resende, Cristina do Amparo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Luís Roberto Marcondes, 1960-, Sundfeld, Renato Hermann, Lovadino, José Roberto |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 134p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds