This understanding of nanocellulose can be directly applied in future formulation design to use nanocellulose in polymer nanocomposites, foams, emulsions, latexes, gels and biomedical materials. / In this study, the potential of nanocellulose as a reinforcing agent in composite materials was investigated using atomic force microscopy (AFM). AFM was used to probe the mechanical properties of nanocelluloses and to investigate their interactions and adhesion in liquid media. Amplitude modulated-frequency modulated AFM was used to map the mechanical properties of cellulose nanocrystals (CNCs) and cellulose nanofibrils (CNFs). Results showed Young’s moduli of 90 GPa and 120 GPa for CNCs and CNFs, respectively, which are comparable to literature values determined using other methods.
Additionally, colloid probe AFM was implemented to observe the interactions (attractive, repulsive, steric, adhesive) between cellulose and silica colloid probes with anionic CNCs (containing either a Na+ or H+ counterion) and cationic CNCs. Colloid probe AFM measurements were carried out in five different liquid media: two salt solutions (NaCl and CaCl2) and three surfactant solutions (cationic cetyltrimethylammonium bromide, CTAB; anionic sodium dodecyl sulfate, SDS; and nonionic Triton X100). It was found that low salt concentrations resulted in electrostatic repulsion and high adhesion, whereas the reverse was observed at high salt concentrations. On the contrary, an increased surfactant concentration and increased number of surfactant aggregates (micelles, bilayers, etc.) resulted in increased adhesion. Surprisingly, the interactions were strongly dependent on the CNC counterion as surfactant adsorption seemed to be primarily driven by electrostatic interactions; CTAB adsorbed more to anionic CNCs, SDS adsorbed more to cationic CNCs and Triton X100 adsorbed minimally to all CNCs. Electrophoretic mobility and particle size data showed complementary results to colloid probe AFM, indicating that interactions between surfactants and CNC films and CNCs in suspension are closely related. This research suggests that CNCs have potential as reinforcing agents due to their high strength and the tunability of their interactions through the simple addition of salts or surfactants. This understanding can be directly applied in future formulation design to use nanocellulose in polymer nanocomposites, foams, emulsions, latexes, gels and biomedical materials. / Thesis / Master of Applied Science (MASc) / Nanocellulose is a sustainable nanomaterial most commonly extracted from plants and trees. In recent research, nanocellulose has been shown to have potential as a reinforcing agent for materials such as plastics, foams, paints and adhesives. In this study, the potential of nanocellulose was investigated using atomic force microscopy (AFM). As predicted, AFM measurements indicated that nanocellulose has a high stiffness, supporting the substitution of this biobased material in the place of metals and synthetic fibres. AFM was also used to examine particle interactions in salt and soap-like (surfactant) solutions; changes in nanocellulose size and charge were used to support the findings. Negatively charged nanocellulose interacted more with positively charged surfactants and vice versa. Low salt and high surfactant concentrations led to high adhesion and better material compatibility, which is preferred. This understanding can help us design better nanocellulose materials for future applications.
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/20791 |
| Date | January 2017 |
| Creators | Marway, Heera |
| Contributors | Cranston, Emily, Chemical Engineering |
| Source Sets | McMaster University |
| Language | en_US |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0024 seconds