Previous issue date: 2004 / Resumo: O desenvolvimento de próteses articulares com superfície complacente, capaz de favorecer ou permitir a lubrificação entre os componentes das juntas artificiais, como acontece nas juntas naturais, vem despertando grande interesse visto que diminui o coeficiente de atrito entre as superfícies, favorecendo o deslizamento entre as mesmas e minimizando o desgaste. A proposta deste trabalho foi estudar e melhorar as propriedades mecânicas de hidrogéis poliméricos de poli (metacrilato de 2-hidroxietila) (pREMA) e poli (álcool vinílico) (PVA) reconhecidamente utilizados no estudo de reparadores da cartilagem articular natural. Para tanto foram obtidos copolímeros de pREMA e n-vinil pirrolidona (NVP) (polímero hidrofílico de reforço) variando-se a concentração de agente de reticulação e blendas de poliHEMA com o copolímero poli(metacrilato de metila-co-ácido acrílico) (75:25) enquanto que, os hidrogéis a base de poli (álcool vinílico) foram reticulados com radiação ionizante de feixe de elétrons. O estudo envolveu a caracterização térmica, mecânica e morfológica desses materiais bem como sua caracterização quanto ao desgaste em um equipamento do tipo PIN-ON-DISK com uma contra-superficie de metal em condições próximas à fisiológica com movimento relativo rotativo e, ainda, com movimento recíproco ou alternado / Abstract: There is an increasing interest in the development of soft layered articular prostheses, which favour sliding between components, as natural joints do, thus reducing contact stresses and wear. The purpose of this work was to characterize and improve the mechanical properties of poly (2-hydroxyethyl metacrylate) (pHEMA) and polyvinyl alcohol (PVA) hydrogels. These hydrogels are extensively studied for articular cartilage repair. Samples of pHEMA and n-vinyl pirrolidone (NVP) copolymers with different amounts of trimethylol propane trimethacrylate (TMPTMMA) crosslinking agent, and samples of pHEMA/poly (methyl metacrylate-co-acrylic acid) blends were prepared by thermal polymerization. Additionally, PVA based hydrogels were prepared by means of electron beam ionizing radiation. Hydrogel samples were characterized by indentation creep test, equilibrium water content (EWC) and Differential Scanning Calorimetry (DSC). The tribological characterization of hydrogels was performed under nearly looading physiological conditions at room temperature on a pin-on-disc equipment, Plint TE67, using a stainless steel 316L disc counter surface / Doutorado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263533 |
| Date | 26 July 2004 |
| Creators | Bavaresco, Vanessa Petrilli, 1971- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Reis, Marcelo de Carvalho, 1965-, Zavaglia, Cecília Amélia de Carvalho, 1954-, Zoqui, Eugênio José, Gomes, Jose M. Ramos, Sinatora, Amilton, Malmonge, Sonia Maria |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 143p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0106 seconds